Debridement of Bacterial Biofilms with TiO2/H2O2 Solutions and Visible Light Irradiation
Debridement of Bacterial Biofilms with TiO2/H2O2 Solutions and Visible Light Irradiation
Oscar Janson,1 Maria Strømme,2 Håkan Engqvist,1 and Ken Welch2
1Division of Applied Material Science, Department of Engineering Sciences, Uppsala University, Uppsala 751 21, Sweden
2Division of Nanotechnology and Functional Materials, Department of Engineering Sciences, Uppsala University, Uppsala 751 21, Sweden
Correspondence should be addressed to Oscar Janson; firstname.lastname@example.org
Received 10 April 2018; Accepted 6 June 2018; Published 2 July 2018
Academic Editor: Wen-Cheng Chen
Copyright © 2018 Oscar Janson et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Objectives. The aim of the study was to explore the debridement efficacy of different solutions of H2O2 and rutile particles against Staphylococcus epidermidis and Pseudomonas aeruginosa biofilms attached to titanium surfaces when exposed to visible light. Materials and Methods. Titanium discs cultivated with biofilms of Staphylococcus epidermidis or Pseudomonas aeruginosa were subjected for 1 min to suspensions consisting of rutile particles mixed with high (950 mM) or low (2 mM) concentrations of H2O2 under visible light irradiation (405 nm; 2.1 mW/cm2). Discs were rinsed and the degree of debridement was determined through scanning electron microscopy and viability assessment of the remaining bacteria using luminescence measurements and/or a metabolic activity assay. Results. Cleaning mixtures containing the higher concentration of H2O2 showed a significantly improved debridement compared to the negative control in all experiments. The addition of rutile particles was shown to have a statistically significant effect in one test with S. epidermidis. Limited evidence of the catalytic effect of visible light irradiation was seen, but effects were relatively small and statistically insignificant. Conclusions. H2O2 at a concentration of 950 mM proved to be the strongest contribution to the debridement and bactericidal effect of the cleaning techniques tested in this study.
Peri-implantitis is an inflammatory disease that is defined by bleeding on probing and marginal loss of bone at the implant site . The frequency of peri-implantitis has been reported to be as high as 19-22% of subjects and 9-10% of implants [2–4]. Peri-implantitis arises from bacteria attaching to the dental implants leading to the formation of bacterial biofilms, which are clusters of bacteria encased in an extracellular polymeric substance and adherent to a surface . The bacteria in biofilms possess a different gene expression compared to planktonic bacteria which can make the infection resistant to antibiotics . Therefore nonantibiotic treatment alternatives may be required. Commonly used cleaning protocols for peri-implantitis infected implants include mechanical cleaning with curettes or brushes, which can damage the implant surface and have difficulty reaching bacteria located in the micro roughness of the implants . Chemicals like hydrogen peroxide (H2O2), chlorhexidine gluconate, saline, and citric acid are also used for disinfection and while they all show good effect, they are not satisfactory for complete cleaning of the implants . Therefore there is an urgent need for more effective cleaning methods.
Photocatalytic activation of titanium dioxide (TiO2) has long been investigated not only as an environmental cleaning agent of waste water and air purification , but also for biomedical applications [10–12]. Photocatalysis occurs when an electron from the valence band in a TiO2 crystal is excited to the conduction band by a photon of higher energy compared to the band gap between the valence and conduction bands of the crystal, thereby creating an electron-hole pair. The band gaps for the two most common crystal forms of TiO2, anatase and rutile, are 3.20 and 3.03 eV, respectively , corresponding to light wavelengths of 387 nm and 409 nm, respectively. The excited electron can react with oxygen (O2) and create superoxide radicals () while the hole can react with water (H2O) and give rise to hydroxyl radicals (∙OH) . Reactive oxygen species (ROS) such as hydroxyl radicals, superoxide radicals, and H2O2 are known to damage the cell wall of bacteria leading to cell death . Rutile has a smaller band gap but is considered a less active photocatalyst compared to anatase or mixed anatase/rutile phases . However when adding small amounts of H2O2, rutile has been shown to increase hydroxyl radical formation under light irradiation [16–18]. H2O2 is in itself an effective antiseptic and with a concentration of 3 vol.% (950 mM) has been shown to be an effective treatment against S. epidermidis biofilms on titanium dental implant surfaces in vitro [19–21]. TiO2 in combination with H2O2 has been shown to give rise to an increased synergistic bactericidal effect [19, 21]. Studies have shown that small amounts of H2O2 together with TiO2 of the allotropic form rutile under light exposure is the most effective combination to degrade the organic dye Rhodamine B , as well as inactivate the multiresistant bacterium Klebsiella pneumoniae .
We hypothesize that TiO2 particles combined with H2O2 under light irradiation can be effective in debriding peri-implantitis infected implants. Consequently, the aim of this study was to explore the debridement efficacy of mixtures of rutile TiO2 particles and H2O2 under visible light irradiation (405 nm wavelength) on Staphylococcus epidermidis and Pseudomonas aeruginosa biofilm adherent to Ti surfaces. S. epidermidis is a Gram-positive bacterium that easily can create biofilms  and P. aeruginosa is a Gram-negative, rod-shaped bacterium which has a low antibiotic susceptibility, making this pair suitable for the test in the current study. Both species are facultative anaerobes, which means that they can grow both with and without oxygen.
2. Material and Methods2.1. Titanium Discs
Commercially pure (cp), machine shaped Ti discs (diameter 6.2 mm, thickness 2 mm) were surface-modified to mimic a rough dental implant surface. The discs were grit blasted with TiO2 particles (particle size = 180-220 μm) and further acid etched with 0.2 vol.% hydrofluoric acid. A detailed description of the modification procedure and a detailed characterization of the surface can be found elsewhere .
2.2. Bacteria Strains and Biofilm Formation
Two bacteria strains were selected to form biofilms in this study. First, a genetically modified Gram-positive strain of S. epidermidis XEN 43 was used. The strain was derived from the clinical isolate S. epidermidis 1457, where luxABCDE genes have been incorporated into the bacterial genome to create a constitutive bioluminescent strain. The engineered strain has been shown to be phenotypically equal to its parental strain  and was stored as frozen stock cultures at −20°C in 15% glycerol (American Bioanalytic, Natick, MA, USA) to avoid phenotypic changes due to passages. Tryptic soy broth (TSB) with 10 % glucose syrup (Dan Sukker, Nordic Sugar AB, Malmö, Sweden) was used as growth medium and incubation was performed in an aerobic atmosphere at 37°C. Biofilm inoculum for Ti discs was prepared by adding 10 μl stock to 10 ml growth medium and inoculating overnight before adjusting the OD at 600 nm to 0.02 (~ 1 x 107 cells ml−1). 600 μl of the bacterial suspension was added to Ti discs placed in a 48-well microtiter plate (Nunc, Roskilde, Denmark) and then incubated for 24 h to allow colonization and biofilm formation on the discs. Details on determination of the correlation between luminescence and colony forming units (CFU), as well as OD600 and CFU, can be found elsewhere .
The second bacteria strain used was the Gram-negative, rod-formed bacterial species P. aeruginosa ATCC 39324, which is a mucoid clinical isolate from a cystic fibrosis patient. 200 μl of precultures of P. aeruginosa was added to 10 ml Tryptic soy broth (TSB) with 0.2 % (v/v) of glycerol and inoculated in aerobic conditions in 37°C overnight. Ti discs were then inoculated with 600 μl of bacterial suspension diluted to OD600 = 0.2 and then incubated for 24 h to allow colonization and biofilm formation on the discs.
2.3. Cleaning (Debridement) Procedure
Table 1 details the composition of the sample cleaning mixtures and the treatment conditions. TiO2 particles used were of the allotropic form rutile. As a positive control 70% ethanol was used, prepared from mixing 96% ethanol (VWR, Fontenay-sous-Bois, France) with deionized water. Dulbecco’s phosphate buffered saline with added Mg2+ and Ca2+ (PBS) was used as negative control and also as solvent in cleaning mixtures. All chemicals including the rutile particles were purchased from Sigma Aldrich (Sigma Aldrich, St Louis, MO, USA) if not stated differently.
Table 1: Description of debridement treatment conditions. Exposure time was 1 min for all treatment conditions.
After the biofilm formation procedure detailed in Section 2.2, discs were moved to another 48-well microtiter plate containing a solution with sterile PBS. Before debridement discs with biofilm were washed three times in PBS to remove bacteria that were not attached to a biofilm. This washing procedure was not used within a second set of tests with S. epidermidis discs as it was found that the biofilm had too poor adherence to the surface. From there the discs were transferred to new wells and 200 μl of the chemical agents listed in Table 1 was added. Mixtures containing TiO2 particles were vortexed immediately before use. Treatment was stopped after 1 min by transferring the discs to separate wells filled with 1 ml PBS. Discs were then rinsed by pipetting sterile PBS three times to remove all chemical agents before further processing. All test groups consisted of 9 replicates from which 1 was used for scanning electron microscopy (SEM) assessment.
2.4. Assessment of Debridement and Bacterial Viability2.4.1. Scanning Electron Microscopy
One disc from each test group was removed for examination with SEM. The discs were fixated in 2.5% glutaraldehyde for 1 h, followed by immersion in ethanol (30, 50, 70, and 96% ethanol) for 10 min in each concentration. Subsequently the discs were soaked in hexamethyldisilane (HMDS) for 15 min and then left to dry for a couple of hours. Afterwards the discs were sputter-coated with a thin Au/Pd layer for increased signal and reduced charging effects. The discs were then imaged using the secondary electron detector in a Leo 1530 scanning electron microscope (Zeiss, Oberkochen, Germany) operated at 5.0 kV.
2.4.2. Metabolic Activity Assay (MAA)
The postdebridement viability of both bacterial strains was analyzed using the MAA. 400 μl of MAA solution composed of the metabolic indicator resazurin at a concentration of 12.5 μg/ml in TSB was added to each well containing a sample disc. Fluorescence measurements were made every hour for 6 hours in a Tecan M200 fluorescence spectrometer, with excitation wavelength set at 530 nm and emission wavelength at 590 nm. Between measurements the plates were placed on a shaker board in 37°C. Wells containing only TSB were also measured to determine the background fluorescence, which was then subtracted from all test groups.
2.4.3. Luminescence Measurements
Regrowth of S. epidermidis bacteria was also measured by monitoring luminescence after a separate debridement test. In this test, washing of the discs before the debridement procedure was not performed as it was observed in the previous MAA experiment that prewashing removed too much of the biofilm. After the debridement procedure, eight discs of each group were transferred to a new 48-well plate and the wells were filled with 600 μl of TSB. Luminescence was recorded at the start of regrowth (0 h) and once every hour from 8 h to 18 h after start of regrowth in a Hidex chameleon plate reader. Between measurements the plates were stored at 37°C. A well containing a sterile Ti disc was also measured to ensure that the growth media or Ti substrate did not contribute to the luminescent signal. For comparison of regrowth between sample groups, the time for samples to reach 2000 luminescence units was used.
2.5. Statistical Analysis
The results are presented as the mean ± standard error of the mean. Statistically significant differences from the mean were calculated with one-way ANOVA, followed by Dunnett and Tukey post hoc tests. The Dunnett post hoc test was used to compare each test group against the PBS control while the Tukey post hoc test was used to confirm statistically significant differences amongst the four test groups and positive control. The Anderson-Darling test was used to verify if the data sets were normally distributed and Levene’s test was used to assess the equality of variances.
3. Results3.1. MAA: S. epidermidis
Figure 1 shows the viability of S. epidermidis after the debridement treatments as measured with the MAA. All five test groups exhibited statistically significantly lower fluorescence intensities after 3 h regrowth compared to the PBS treated Ti discs (Figure 1(b)). The positive control discs treated with ethanol showed a strong bactericidal effect in the MAA, but after three-hour reincubation, bacterial growth increased at a higher rate compared to the other groups; cf. Figure 1(a). It can also be seen in the SEM micrographs in Figure 2 that the ethanol treatment did not effectively debride the biofilm as a relatively large amount of bacteria remained on the surface compared to the discs treated with PBS. On the other hand, the R_Hi_Li treatment appeared to have produced the most efficient debridement as very few bacterial cells could be observed on the disc surface, which was also supported by the lowest fluorescence values recorded in the MAA. However, it should be noted that due to the relatively poor adhesion of the S. epidermidis biofilm to the discs, a large percentage of the bacteria was removed from all discs during the washing procedure before debridement, which likely contributed to the high variability in the recorded data. Consequently, the lower viability of R_Hi_Li compared to 0_Hi_Amb and R_Hi_Amb in Figure 1(b) was not statistically significant (Tukey post hoc test, p≤ 0.05).
Figure 1: Regrowth of S. epidermidis after different debridement treatments. Background fluorescence from TSB was subtracted from all test groups. (a) Average fluorescence intensity measured during reincubation after debridement with different treatments (n=8). (b) Average fluorescence intensity after 3 h regrowth. Groups with an asterisk indicate statistically significant difference compared to the control PBS (Dunnett post hoc test, p≤ 0.05). Groups with different letters are significantly different (five test groups compared, Tukey post hoc test, p ≤ 0.05).
Figure 2: SEM micrographs of S. epidermidis on the Ti surfaces after the different debridement treatments.
3.2. Luminescence Assay: S. epidermidis
Figure 3 displays the viability of S. epidermidis postdebridement treatment, as measured with the luminescence assay. As can be seen in panel (a), the negative control (i.e., PBS treatment) and R_Low_Li samples had the highest viability and both showed a peak in the regrowth curve at approximately 8 h (note that luminescence measurements were not made between the initial measurement at 0 h, just after the cleaning treatments, and 8 h). The positive control (ethanol) had an earlier/faster regrowth than the test groups containing higher concentrations of H2O2, which may be expected since the previous MAA with S. epidermidis showed that the activity or growth of bacteria on the ethanol discs increased at an accelerated rate after three hours of reincubation. Because luminescence measurements were not taken between the initial measurement at 0 h and 8 h, it is not possible to assess the viability of the ethanol discs compared with the other sample groups in this period.
Figure 3: Regrowth of S. epidermidis after different debridement treatments. (a) Average luminescence intensity measured during reincubation after debridement with different treatments (n=8). (b) Average time after reincubation to reach a luminescence intensity unit of 2000 for four of the test groups. Different letters associated with the bars indicate statistically significant differences (Tukey post hoc test, p ≤ 0.05).
Similar to the previous MAA, Figure 4 shows that a relatively large amount of bacteria remained on the ethanol discs, suggesting that while ethanol treatment kills or inactivates the bacteria, it does not debride the biofilm. Note that the washing procedure before debridement was not performed in this test, which is why, relatively, so many more bacteria are observed in Figure 4 compared to Figure 2.
Figure 4: SEM micrographs of S. epidermidis on the Ti surfaces after the different debridement treatments.
Figure 4 also shows that the debridement treatment with high H2O2 concentrations resulted in efficient debridement of the S. epidermidis biofilm, which is supported by luminescence measurements. The addition of TiO2 particles to the H2O2 solutions yielded a significant delay in regrowth time; cf. Figure 3(b). However, irradiation with 405 nm light did not seem to have additional benefits as was suggested by the trend in the MAA measurements.
3.3. MAA: P. aeruginosa
Figure 5 displays the viability of P. aeruginosa after the debridement treatments as measured with the MAA. The Ti discs treated with debridement solutions containing the higher concentration of H2O2 all showed a significantly lower fluorescence signal at six hours after debridement compared to the Ti discs treated with only PBS; see Figure 5(b). An assessment time of 6 h was chosen instead of 3 h as was used with S. epidermidis due to the relatively slower growth rate of the P. aeruginosa bacteria. It is notable that the positive control ethanol did not show a significantly lower signal than PBS at 6 h, but this is likely due to an increased activity or growth rate after an initial period of reincubation as was seen with S. epidermidis. Inspection of the viability curves in Figure 5(a) gives the fact that the viability of the ethanol group is in fact the lowest for the first three hours of reincubation. Figure 6 displays SEM micrographs of the Ti surfaces after the debridement treatments, which show a very different morphology of the P. aeruginosa biofilm compared with the S. epidermidis biofilm. Figure 6 as well shows that a substantial amount of rutile particles is left after the debridement treatment.
Figure 5: Regrowth of P. aeruginosa after different debridement treatments. (a) Fluorescence measured during reincubation after debridement with different treatments (n=8). (b) Average fluorescence intensity after 6 h regrowth. Groups with an asterisk indicate statistically significant difference compared to the control PBS (Dunnett post hoc test, p≤ 0.05). Groups with different letters are significantly different (five test groups compared, Tukey post hoc test, p ≤ 0.05).
Figure 6: SEM micrographs of P. aeruginosa on the Ti surfaces after the different debridement treatments.
In this study the antibacterial effect and debridement efficacy of mixtures of H2O2 and TiO2 particles with and without visible light irradiation was performed on S. epidermidis and P. aeruginosa biofilms grown on Ti surfaces. The choice of the Gram-positive S. epidermidis was made because of its good biofilm forming abilities and this special strain Xen 43 provides the ability to monitor viability using luminescence measurements, giving a direct indication of bacterial proliferation [21, 24]. P. aeruginosa was chosen because it is a Gram-negative strain, which generally has a stronger resistance against antimicrobials . The higher H2O2 concentration of 950 mM (3 vol.%) was chosen because it is used clinically today to debride peri-implantitis infected implants while the lower concentration of 2 mM (0.006 vol.%) was chosen because it has been shown to be the optimal concentration to degrade an organic substance when combined with rutile particles under visible light irradiation .
It was observed that the debridement mixtures with high concentrations of H2O2 (950 mM) produced a large bubbling effect when applied on the biofilm-covered surface. The high reduction of biofilm associated with high concentrations of H2O2 seen in the S. epidermidis test assessed with luminescence may thus be correlated to the oxygen evolution evidenced by the bubbles that are formed [19–21]. These bubbles are caused by H2O2 being decomposed by catalase produced by the bacteria. The bubbles in turn may create mechanical forces in the solution that remove the attached bacteria. This effect was most apparent in the luminescence test with S. epidermidis because more bacteria were present on the surface prior to the debridement treatments compared to the MAA test with S. epidermidis. The first debridement test using S. epidermidis showed that the bacteria were poorly attached to the Ti surface since a large proportion was removed with just a gentle rinsing with PBS prior to the debridement treatment, and thus this prewash was not performed with the luminescence test. With the addition of rutile particles there was an increased bactericidal effect when measured with luminescence, possibly because the particles added an extra mechanical force to the bubbling effect, which is in line with several other studies [19, 21]. However, it could also be due to a catalytic effect of the rutile particles on H2O2 to generate additional ROS [19, 21].
The addition of light irradiation at a wavelength of 405 nm did not provide a statistically significant extra effect, although a trend for increased effect was seen in the MAA tests with both bacteria species when combined with a high H2O2 concentration. Theoretically this wavelength has enough energy to induce photocatalysis in the rutile particles used in this study, which could produce additional ROS. The lack of a clear effect may be because hydroxyl radicals, which are the main bactericidal ROS created in photocatalysis, are very reactive and consequently would have a reaction distance in the magnitude of micrometers [10, 21]. This would limit the effect to the immediate surroundings of the particles, which may not be close enough to the majority of the bacteria based on the particle concentrations used in this study. In the luminescence experiments, no effect of irradiation was seen, but this may partially be due to the fact that the mechanical debridement from the evolved oxygen bubbles removed the majority of the biofilm and with it the overlaying rutile particles.
Ethanol had a stronger effect on S. epidermidis in the MAA experiment compared to P. aeruginosa. The smaller effect against P. aeruginosa is expected since this strain is more resistant against ethanol compared to S. epidermidis . In all tests, biofilms treated with ethanol showed an increased activity or regrowth after a delay period during reincubation. This highlights the advantages of the other debridement treatments used in this study.
In summary, H2O2 at a concentration of 950 mM proved to be the strongest contribution to the debridement and bactericidal effect of the cleaning techniques tested in this study. The addition of rutile particles may have additional benefit and was shown to have a statistically significant effect in one test with S. epidermidis. Limited evidence of the catalytic effect of visible light irradiation was seen, but effects were relatively small and statistically insignificant. Further studies with clinically relevant and multispecies biofilm should be performed to confirm these results. The debridement of dental implants with H2O2 and rutile particles under visible light irradiation can be used as an alternative or complementary technique to presently used methods such as mechanical debridement or chemical disinfection in the treatment of peri-implantitis.
The data used to support the findings of this study are included within the article.
Conflicts of Interest
The authors declare that they have no conflicts of interest.
The authors acknowledge David Wiedmer (Department of Biomaterials, Oslo University) for grit blasting and acid etching of the Ti discs, as well as providing S. epidermidis Xen 43 at no cost. This research was funded by Vinnova, Sweden’s innovation agency, through the Eurostar program Eureka, Grant no. [E!8320].
References N. P. Lang, T. Berglundh, and Working Group 4 of the Seventh European Workshop on Periodontology, “Periimplant diseases: where are we now?—consensus of the Seventh European Workshop on Periodontology,” Journal of Clinical Periodontology, vol. 38, supplement 11, pp. 178–181, 2011. View at Publisher · View at Google Scholar · View at ScopusM. A. Atieh, N. H. M. Alsabeeha, C. M. Faggion Jr., and W. J. Duncan, “The frequency of peri-implant diseases: a systematic review and meta-Analysis,” Journal of Periodontology, vol. 84, no. 11, pp. 1586–1598, 2013. View at Publisher · View at Google Scholar · View at ScopusC.-T. Lee, Y.-W. Huang, L. Zhu, and R. Weltman, “Prevalences of peri-implantitis and peri-implant mucositis: systematic review and meta-analysis,” Journal of Dentistry, vol. 62, pp. 1–12, 2017. View at Publisher · View at Google Scholar · View at ScopusJ. Derks and C. Tomasi, “Peri‐implant health and disease. A systematic review of current epidemiology,” Journal of Clinical Periodontology, vol. 42, supplement 16, pp. S158–S171, 2015. View at Publisher · View at Google ScholarA. Han, J. K. H. Tsoi, F. P. Rodrigues, J. G. Leprince, and W. M. Palin, “Bacterial adhesion mechanisms on dental implant surfaces and the influencing factors,” International Journal of Adhesion and Adhesives, vol. 69, pp. 58–71, 2016. View at Publisher · View at Google Scholar · View at ScopusJ. W. Costerton, P. S. Stewart, and E. P. Greenberg, “Bacterial biofilms: a common cause of persistent infections,” Science, vol. 284, no. 5418, pp. 1318–1322, 1999. View at Publisher · View at Google Scholar · View at ScopusG. R. Persson, E. Samuelsson, C. Lindahl, and S. Renvert, “Mechanical non-surgical treatment of peri-implantitis: A single-blinded randomized longitudinal clinical study. II. Microbiological results,” Journal of Clinical Periodontology, vol. 37, no. 6, pp. 563–573, 2010. View at Publisher · View at Google Scholar · View at ScopusR. Bürgers, C. Witecy, S. Hahnel, and M. Gosau, “The effect of various topical peri-implantitis antiseptics on Staphylococcus epidermidis, Candida albicans, and Streptococcus sanguinis,” Archives of Oral Biolog, vol. 57, no. 7, pp. 940–947, 2012. View at Publisher · View at Google Scholar · View at ScopusM. R. Hoffmann, S. T. Martin, W. Y. Choi, and D. W. Bahnemann, “Environmental applications of semiconductor photocatalysis,” Chemical Reviews, vol. 95, no. 1, pp. 69–96, 1995. View at Publisher · View at Google Scholar · View at ScopusY. Cai, M. Strømme, A. Melhus, H. Engqvist, and K. Welch, “Photocatalytic inactivation of biofilms on bioactive dental adhesives,” Journal of Biomedical Materials Research Part B: Applied Biomaterials, vol. 102, no. 1, pp. 62–67, 2014. View at Publisher · View at Google Scholar · View at ScopusE. Unosson, E. K. Tsekoura, H. Engqvist, and K. Welch, “Synergetic inactivation of Staphylococcus epidermidis and Streptococcus mutansin a TiO2/H2O2/UV system,” Biomatter, vol. 3, no. 4, 2013. View at Publisher · View at Google Scholar · View at ScopusF. Rupp, M. Haupt, H. Klostermann et al., “Multifunctional nature of UV-irradiated nanocrystalline anatase thin films for biomedical applications,” Acta Biomaterialia, vol. 6, no. 12, pp. 4566–4577, 2010. View at Publisher · View at Google Scholar · View at ScopusD. O. Scanlon, C. W. Dunnill, J. Buckeridge et al., “Band alignment of rutile and anatase TiO2,” Nature Materials, vol. 12, no. 9, pp. 798–801, 2013. View at Publisher · View at Google Scholar · View at ScopusA. Fujishima, X. Zhang, and D. A. Tryk, “TiO2 photocatalysis and related surface phenomena,” Surface Science Reports, vol. 63, no. 12, pp. 515–582, 2008. View at Publisher · View at Google Scholar · View at ScopusP. C. Maness, S. Smolinski, D. M. Blake, Z. Huang, E. J. Wolfrum, and W. A. Jacoby, “Bactericidal activity of photocatalytic TiO2 reaction: Toward an understanding of its killing mechanism,” Applied and Environmental Microbiology, vol. 6, pp. 4094–4098, 1999. View at Publisher · View at Google ScholarY. Kakuma, A. Y. Nosaka, and Y. Nosaka, “Difference in TiO,” Physical Chemistry Chemical Physics, vol. 17, no. 28, pp. 18691–18698, 2015. View at Publisher · View at Google ScholarT. Hirakawa, K. Yawata, and Y. Nosaka, “Photocatalytic reactivity for O2∙ and OH∙ radical formation in anatase and rutile TiO2 suspension as the effect of H2O2 addition,” Applied Catalysis A: General, vol. 325, pp. 105–111, 2007. View at Google ScholarJ. Zhang and Y. Nosaka, “Mechanism of the OH Radical Generation in Photocatalysis with TiO,” The Journal of Physical Chemistry C, vol. 118, no. 20, pp. 10824–10832, 2014. View at Publisher · View at Google ScholarE. Henderson, S. Schneider, F. C. Petersen et al., “Chemical debridement of contaminated titanium surfaces: An in vitro study,” Acta Odontologica Scandinavica, vol. 71, no. 3-4, pp. 957–964, 2013. View at Publisher · View at Google Scholar · View at ScopusE. Gustumhaugen, J. Lönn-Stensrud, A. A. Scheie, S. P. Lyngstadaas, A. Ekfeldt, and S. Taxt-Lamolle, “Effect of chemical and mechanical debridement techniques on bacterial re-growth on rough titanium surfaces: An in vitro study,” Clinical Oral Implants Research, vol. 25, no. 6, pp. 707–713, 2014. View at Publisher · View at Google Scholar · View at ScopusD. Wiedmer, F. C. Petersen, J. Lönn-Stensrud, and H. Tiainen, “Antibacterial effect of hydrogen peroxide-titanium dioxide suspensions in the decontamination of rough titanium surfaces,” Biofouling, vol. 33, no. 6, pp. 451–459, 2017. View at Publisher · View at Google Scholar · View at ScopusO. Janson, E. Unosson, M. Strømme, H. Engqvist, and K. Welch, “Organic degradation potential of a TiO2/H2O2/UV–vis system for dental applications,” Journal of Dentistry, vol. 67, pp. 53–57, 2017. View at Publisher · View at Google Scholar · View at ScopusL. Korösi, M. Prato, A. Scarpellini et al., “H2O2-assisted photocatalysis on flower-like rutile TiO2 nanostructures: Rapid dye degradation and inactivation of bacteria,” Applied Surface Science, vol. 365, pp. 171–179, 2016. View at Publisher · View at Google Scholar · View at ScopusC. Vuong, S. Kocianova, J. Yu, J. L. Kadurugamuwa, and M. Otto, “Development of real-time in vivo imaging of device-related Staphylococcus epidermidis infection in mice and influence of animal immune status on susceptibility to infection,” The Journal of Infectious Diseases, vol. 198, no. 2, pp. 258–261, 2008. View at Publisher · View at Google Scholar · View at ScopusP. S. Stewart and J. W. Costerton, “Antibiotic resistance of bacteria in biofilms,” The Lancet, vol. 358, no. 9276, pp. 135–138, 2001. View at Publisher · View at Google Scholar · View at ScopusP. D. Lister, D. J. Wolter, and N. D. Hanson, “Antibacterial-resistant Pseudomonas aeruginosa: clinical impact and complex regulation of chromosomally encoded resistance mechanisms,” Clinical Microbiology Reviews, vol. 22, no. 4, pp. 582–610, 2009. View at Publisher · View at Google Scholar · View at Scopus