Efficiency Enhancement of Perovskite Solar Cells by Pumping Away the Solvent of Precursor Film Before Annealing

Nanoscale Research Letters, May 2016

A new approach to improve the quality of MAPbI3 − x Cl x perovskite film was demonstrated. It involves annealing the precursor film after pumping away the solvent, which can decrease the influence of solvent evaporation rate for the growth of the MAPbI3 − x Cl x perovskite film. The resulting film showed improved morphology, stronger absorption, fewer crystal defects, and smaller charge transfer resistance. The corresponding device demonstrated enhanced performance when compared with a reference device. The averaged value of power conversion efficiency increased from 10.61 to 12.56 %, and a champion efficiency of 14.0 % was achieved. This work paves a new way to improve the efficiency of perovskite solar cells.

A PDF file should load here. If you do not see its contents the file may be temporarily unavailable at the journal website or you do not have a PDF plug-in installed and enabled in your browser.

Alternatively, you can download the file locally and open with any standalone PDF reader:

https://link.springer.com/content/pdf/10.1186%2Fs11671-016-1467-9.pdf

Efficiency Enhancement of Perovskite Solar Cells by Pumping Away the Solvent of Precursor Film Before Annealing

Xu et al. Nanoscale Research Letters Efficiency Enhancement of Perovskite Solar Cells by Pumping Away the Solvent of Precursor Film Before Annealing Qing-Yang Xu 0 Da-Xing Yuan 0 Hao-Ran Mu 0 Femi Igbari 0 Qiaoliang Bao 0 Liang-Sheng Liao 0 0 Jiangsu Key Laboratory for Carbon-Based Functional Materials and Devices, Institute of Functional Nano & Soft Materials (FUNSOM), Soochow University , Suzhou, Jiangsu 215123 , China A new approach to improve the quality of MAPbI3 − xClx perovskite film was demonstrated. It involves annealing the precursor film after pumping away the solvent, which can decrease the influence of solvent evaporation rate for the growth of the MAPbI3 − xClx perovskite film. The resulting film showed improved morphology, stronger absorption, fewer crystal defects, and smaller charge transfer resistance. The corresponding device demonstrated enhanced performance when compared with a reference device. The averaged value of power conversion efficiency increased from 10.61 to 12.56 %, and a champion efficiency of 14.0 % was achieved. This work paves a new way to improve the efficiency of perovskite solar cells. Perovskite solar cells; Pump away the solvent; High-quality MAPbI3 − xClx layer Background Organo-metal halide perovskite solar cell, as a rising star in the field of thin-film photovoltaic cells, has drawn much attention, not only due to the superior optical and electrical properties of perovskite materials, such as broad light absorption range [ 1 ], low exciton binding energy [ 2, 3 ], longer carrier diffusion length [ 4–6 ], and higher charge carrier mobilities [7], but also due to its low cost and easy fabrication process. The first work employing perovskite as a light-harvesting material in solar cells was reported by Miyasaka and co-workers in 2009 with an efficiency of only 3.8 % [ 1 ]. Almost double of this efficiency (6.5 %) was reported by Park’s research group in 2011 [ 8 ]. Due to the dissolubility of perovskite in liquid electrolyte, devices in both works showed poor stability. When a solid-state hole conductor of 2,2′,7,7′-tetrakis(N,N-di-p-methoxyphenylamine)-9,9′spirobifluorene (Spiro-OMeTAD) was introduced to replace the liquid electrolyte, both stability and performance were improved dramatically [ 9 ]. Amazing progress has been made in recent times [ 5, 10–18 ] as a champion efficiency over 20 % has been reported for perovskite-based solar cell [19], making it an ideal candidate for nextgeneration photovoltaic cells. The development of perovskite solar cells came with the challenge of controlling the morphology of the perovskite layer. Such morphology is strongly influenced by several parameters such as fabrication method [ 5, 12, 13, 15, 20–22 ], additives [ 15, 23–26 ], and annealing process [ 16, 27–31 ]. Hence, efforts have been made to improve the morphology of the perovskite layer. For example, Snaith’s group introduced a dual-source thermal evaporation technique [13]. They obtained a much compact and uniform MAPbI3 − xClx perovskite layer compared with the traditional one-step spin-coating method. Liang et al. added a small amount of 1,8-diiodooctane (DIO) to the MAPbI3 − xClx precursor solution and found that a high-quality MAPbI3 − xClx perovskite film was formed with improved coverage and absorption. As a result, the power conversion efficiency (PCE) was increased by 20 % [ 23 ]. Yang Yang et al. investigated the influence of annealing conditions on the perovskite layer. They annealed the precursor film in a humid environment (~30 %) which greatly improved the film quality, grain size, carrier mobility, and lifetime. This method produced planar devices with a pretty high PCE approaching 17.1 % [ 16 ]. Rira et al. found that a solvent evaporation rate can strongly influence the growth of the MAPbI3 − xClx perovskite film. By controlling the solvent evaporation rate, they obtained a MAPbI3 − xClx perovskite layer with improved surface coverage. Thus, improved performance was achieved [ 28 ]. In this letter, we report a new approach to obtain a highquality MAPbI3 − xClx perovskite layer, by pumping away the solvent of precursor film before annealing to decrease the influence of solvent evaporation rate on the growth of MAPbI3 − xClx perovskite film. This approach was proven to be effective as a compact and uniform perovskite film with stronger absorption, fewer crystal defects, and smaller charge transfer resistance. Devices based on this highquality perovskite film showed enhanced performance compared with the reference device. The averaged efficiency increased from 10.61 to 12.56 % and a champion PCE of 14.0 % was achieved. Methods Materials Methylammonium iodide (MAI) was synthesized by reacting 10 ml of hydroiodic acid (57 wt.% in water, Alfa Aesar) with 24 ml of methylamine (33 wt.% in ethanol, Sigma-Aldrich) in ice bath under nitrogen atmosphere with constant stirring. After reacting for 2 h, the resulting white powder of MAI was collected by rotary evaporator at 50 °C. The MAI was dissolved into ethanol and evaporated for further purification. This step was repeated two times, and the MAI powder was finally collected and dried in a vacuum oven at 60 °C for 30 h. Poly(3,4-ethylenedioxythiophene):poly(p-styrene sulfonate) (PEDOT:PSS, Clevios AI 4083) and [ 6,6 ]phenyl-C60-butyric acid methylester (PC60BM) were bought from Heraeus (Germany) and Nichem Fine Technology Co. Ltd. (Taiwan), respectively. To prepare MAPbI3 − xClx (30 wt.%) precursor solution, MAI and PbCl2 (Sigma-Aldrich) were dissolved into N,Ndimethylformamide (DMF) solvent with a molar ratio of 1:1 under constant stirring. The concentration of PC60BM solution was 20 mg/ml in chlorobenzene. Device Fabrication ITO-coated glass substrates with a sheet resistance of ~10 Ω sq−1 were sequentially pre-cleaned by acetone, ethanol, and deionized water and dried by oven. After ultraviolet ozone treatment for 15 min, PEDOT:PSS was spin-coated on the ITO surface at 4000 rpm for 40 s. After annealing at 140 °C for 15 min, the substrates were transferred into a nitrogen-filled glove box. The MAPbI3 − xClx precursor solution was spin-coated on the PEDOT:PSS surface at 4000 rpm for 40 s. For the reference device, the MAPbI3 − xClx perovskite crystal film was achieved by annealing the precursor film directly (100 °C/2 h). While for the modified device, the MAPbI3 − xClx perovskite crystal film was achieved by annealing the precursor film after pumping away the solvent, as shown in Fig. 1 (i.e., pumping the solvent component of the precursor film in the transfer chamber of the glove box for 1 h and then annealing at 100 °C for 2 h). As for the solvent removal process, actually, there exists a mechanical pump, which was connected to the transfer chamber. When opening the mechanical pump, the solvent of the precursor film will be pumped away. After cooling down to room temperature, PC60BM solution was spin-coated on the perovskite layer at 2000 rpm/30 s without further annealing. Finally, a 100-nm-thick silver cathode was evaporated on top of PC60BM by utilizing an OMVFS300 thermal evaporator. The active area of the devices (7.25 mm2) was defined through a shadow mask. Measurements and Characterization Current density-voltage (J-V) characteristics of perovskite solar cells were measured in air using a programmable Keithley 2400 source meter under AM1.5G solar irradiation at 100 mW/cm2 (Newport, Class AAA solar simulator, 94023A-U). The light intensity was calibrated by a certified Oriel Reference Cell (91150 V) and verified with an NRELcalibrated Hamamatsu S1787-04 diode. The external quantum efficiency (EQE) was measured by a certified IPCE instrument (Zolix Instruments, Inc., Solar Cell Scan 100). We utilized a field emission scanning electron microscope (FEI Quanta 200) to investigate the morphology of the perovskite layer. The absorption spectra were measured with a UV/vis spectrophotometer (PerkinElmer Lambda 750). The steady-state photoluminescence spectra were measured by utilizing Horiba Jobin-Yvon LabRAM HR800. Impedance spectroscopy (IS) measurements were performed using a Wayne Kerr 6550B precision impedance analyzer with a 50-mV perturbation oscillation signal in a frequency range from 20 Hz to 20 MHz. Results and Discussion Figure 2a shows the device structure in which PEDOT:PSS and PCBM act as hole and electron transporting layers, respectively. The reference device, in which the MAPbI3 − xClx perovskite layer was obtained by directly annealing the precursor film, and the modified device, in which the MAPbI3 − xClx perovskite layer was obtained by annealing the precursor film after pumping away the solvent, were both measured in air under AM 1.5G solar illumination at 100 mW/cm2. The corresponding current density-voltage (J-V) curve and photovoltaic parameters are shown in Fig. 2b and Table 1. As presented from the data, the reference device, the MAPbI3 − xClx perovskite layer was obtained by directly annealing the precursor film, resulting in an efficiency of 10.61 %. When the MAPbI3 − xClx perovskite layer was obtained by annealing the precursor film after pumping away the solvent, an enhanced performance was achieved with a PCE of 12.59 %, corresponding to an open-circuit voltage (Voc) of 0.91, a short circuit current density (Jsc) of 19.37 mA/cm2, and a fill factor (FF) of 0.71. In addition, the modified device showed smaller series resistance (Rs) and larger shunt resistance (Rsh) which is consistent with the increase in FF. The external quantum efficiency (EQE) for both devices was also measured, as shown in Fig. 2c. We can observe that both devices generated photocurrent up to 800 nm, which corresponds to a bandgap of 1.55 eV. The modified device showed an enhanced EQE spectrum in the range of 400–800 nm. The enhanced EQE value is consistent with the increase in Jsc. From the current density-voltage curves of both the reference and modified devices measured in dark condition (Additional file 1: Figure S1), we find that the leakage current of the modified device is almost one magnitude smaller than that of the reference device. This result indicates that more photocurrent was transported to the electrodes in the modified device. For devices based on the perovskite layer that was annealed after pumping away the solvent of the precursor film, we achieved a champion efficiency of 14.0 % with a Voc of 0.93 V, Jsc of 19.94 mA/cm2, and a FF of 0.76 as shown in Fig. 3a. From the PCE histogram of 40 modified devices, shown in Fig. 3b, it is obvious that the modified device also showed good reproducibility. In order to investigate the hysteresis properties of our modified device, we measured a representative modified device in both forward and reverse directions. As depicted from Additional file 1: Figure S2 and Table S1, when the device was measured in the forward direction, a PCE of 12.64 % was achieved. When we changed the scan direction to reverse mode, the device showed an efficiency of 13.58 %. Noticeably, our modified device possesses small hysteresis properties. The hysteresis effect is so small, which is possibly because of the good crystallinity of the MAPbI3 − xClx perovskite film. As for the origin of the anomalous hysteresis in perovskite solar cells, three major contributions have been suggested: (a) defects located at surfaces or interfaces of the perovskite materials, (b) ferroelectric properties of perovskite structures, and (c) ion migration due to excess ions that serve as interstitial defects. Even though numerous efforts have been made, it is still not clearly understood presently [ 32 ]. In order to understand the reasons behind the improvement of device performance, we carried out SEM, UV-vis absorption, steady-state photoluminescence spectra, and impedance spectroscopy measurements on the perovskite layers and the corresponding devices. Initially, we investigated the surface properties of the perovskite layers prepared by both methods. The SEM images are shown in Fig. 4. When the MAPbI3 − xClx precursor film was annealed directly (Fig. 4a), larger pinholes appeared. We can see that the coverage ratio is pretty low. This will obviously result in poor device performance. When we annealed the MAPbI3 − xClx perovskite precursor film after pumping away the solvent, the perovskite layer becomes much more compact and uniform (Fig. 4b). Full surface coverage was obtained, which is beneficial for device performance. We also measured their absorption properties (Fig. 4c). Due to the low coverage ratio of the perovskite layer achieved by direct annealing, light was able to pass through the large pinholes and weaken the absorption. While for the perovskite layer prepared by annealing the precursor film after pumping away the solvent, a stronger absorption was obtained. This distinctly results in higher external quantum efficiency and Jsc, hence an improved device performance. Figure 5a shows the steady-state photoluminescence spectra of both perovskites on the ITO/PEDOT:PSS surface, prepared by annealing the precursor film directly and by annealing the precursor film after pumping away the solvent. Noticeably, the MAPbI3 − xClx perovskite achieved by annealing the precursor film after pumping away the solvent showed much stronger photoluminescence intensity. It implies that the non-radiative decay is significantly suppressed through our new method. This can effectively reduce the number of crystal defects, thus resulting in fewer carrier recombination and better charge extraction. We also utilized IS to investigate the series resistance (Rs) of both devices. The Rs consists of sheet resistance (Rsheet) of the electrodes and charge transfer resistance (RCT). The following three parts contribute to the RCT: the interfaces between electrodes and charge extraction layer, the interfaces between charge extraction layer, and perovskite layer as well as the bulk of the perovskite layer [ 33 ]. Figure 5b shows the Nyquist plots of both devices tested under applied voltage conditions approaching the Voc of perovskite solar cells. Rs values of 4.9 and 2.8 kΩ were obtained for the reference and modified devices, respectively. Noticeably, the modified device showed much smaller Rs. Since the main difference is located at the perovskite layer in this study, it indicates that the MAPbI3 − xClx perovskite layer prepared by annealing the precursor film after pumping away the solvent exhibits much smaller RCT. Enhanced performance was therefore obtained for the modified device. Conclusions A new approach which involves the annealing of a precursor film after pumping away its solvent component was introduced to obtain a high-quality MAPbI3 − xClx perovskite film. The device based on such high-quality film showed enhanced performance compared with the reference device. The averaged efficiency increased from 10.61 to 12.56 %, and a champion efficiency of 14.0 % was achieved. SEM, UV-vis absorption, steady-state photoluminescence spectra, and impedance spectroscopy results indicated that the improvement in device efficiency is mainly attributed to the improved morphology, stronger absorption, and fewer crystal defects as well as smaller charge transfer resistance of the modified MAPbI3 − xClx perovskite film. This work paves a new way to improve the efficiency of perovskitebased solar cells. Additional File Additional file 1: J-V curves of both the reference and modified devices measured in dark condition. J-V curves and photovoltaic parameters of a modified MAPbI3 − xClx-based device scanned in both forward and reverse directions. Device stability of both reference and modified devices measured in air (humidity: ~40 %, temperature: ~20 °C). Competing Interests The authors declare that they have no competing interests. Authors’ Contributions Q-YX conceived the idea of this paper, participated in the fabrication of the solar cells and wrote the manuscript. D-XY contributed to the experimental processes, measurements, and data analysis. H-RM and FI contributed to the data analysis and manuscript modification. QB and L-SL guided the whole processes. The manuscript was written through the contributions from all the authors. All authors have given approval to the final version of the manuscript. Authors’ Information Qing-Yang Xu, Da-Xing Yuan, and Hao-Ran Mu are graduate students major in optoelectronic materials and devices. Femi Igbari is a PhD student major in nano-materials and devices. Qiaoliang Bao is a professor specializing in optoelectronic materials and devices. Liang-Sheng Liao is a professor specializing in semiconductor devices and physics. Acknowledgements We acknowledge financial support from the Youth 973 Program (Grant No. 2015CB932700), the National Natural Science Foundation of China (Grant No. 51290273, 91433107, and 61177016), and the Natural Science Foundation of Jiangsu Province (Grant No. BK20130288). This project is also funded by the Collaborative Innovation Center of Suzhou Nano Science and Technology and by the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD). Submit your manuscript to a journal and benefit from: 7 Convenient online submission 7 Rigorous peer review 7 Immediate publication on acceptance 7 Open access: articles freely available online 7 High visibility within the field 7 Retaining the copyright to your article 1. Kojima A , Teshima K , Shirai Y , Miyasaka T ( 2009 ) Organometal halide perovskites as visible-light sensitizers for photovoltaic cells . J Am Chem Soc 131 : 6050 - 6051 2. Miyata A , Mitioglu A , Plochocka P , Portugall O , Wang JTW , Stranks SD , Snaith HJ , Nicholas RJ ( 2015 ) Direct measurement of the exciton binding energy and effective masses for charge carriers in organic-inorganic trihalide perovskites . Nat Phys 11 : 582 - 587 3. Lin Q , Armin A , Nagiri RCR , Burn PL , Meredith P ( 2015 ) Electro-optics of perovskite solar cells . Nat Photon 9 : 106 - 112 4. Stranks SD , Eperon GE , Grancini G , Menelaou C , Alcocer MJ , Leijtens T , Herz LM , Petrozza A , Snaith HJ ( 2013 ) Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber . Science 342 : 341 - 344 5. Nie W , Tsai H , Asadpour R , Blancon J-C , Neukirch AJ , Gupta G , Crochet JJ , Chhowalla M , Tretiak S , Alam MA , Wang H-L , Mohite AD ( 2015 ) Highefficiency solution-processed perovskite solar cells with millimeter-scale grains . Science 347 : 522 - 525 6. Dong Q , Fang Y , Shao Y , Mulligan P , Qiu J , Cao L , Huang J ( 2015 ) Electronhole diffusion lengths >175 m in solution-grown CH3NH3PbI3 single crystals . Science 347 : 967 - 970 7. Wehrenfennig C , Eperon GE , Johnston MB , Snaith HJ , Herz LM ( 2014 ) High charge carrier mobilities and lifetimes in organolead trihalide perovskites . Adv Mater 26 : 1584 - 1589 8. Im J-H , Lee C-R , Lee J-W , Park S-W, Park N-G ( 2011 ) 6.5% efficient perovskite quantum-dot-sensitized solar cell . Nanoscale 3 : 4088 - 4093 9. Kim H-S , Lee C-R , Im J-H , Lee K-B , Moehl T , Marchioro A , Moon S-J , Humphry-Baker R , Yum J-H , Moser JE , Gratzel M , Park N-G ( 2012 ) Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9 % . Sci Rep 2 : 591 10. Lee MM , Teuscher J , Miyasaka T , Murakami TN , Snaith HJ ( 2012 ) Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites . Science 338 : 643 - 647 11. Ball JM , Lee MM , Hey A , Snaith HJ ( 2013 ) Low-temperature processed meso-superstructured to thin-film perovskite solar cells . Energy Environ Sci 6 : 1739 - 1743 12. Burschka J , Pellet N , Moon S-J , Humphry-Baker R , Gao P , Nazeeruddin MK , Grätzel M ( 2013 ) Sequential deposition as a route to high-performance perovskite-sensitized solar cells . Nature 499 : 316 - 319 13. Liu M , Johnston MB , Snaith HJ ( 2013 ) Efficient planar heterojunction perovskite solar cells by vapour deposition . Nature 501 : 395 - 398 14. Liu D , Kelly TL ( 2014 ) Perovskite solar cells with a planar heterojunction structure prepared using room-temperature solution processing techniques . Nature Photon 8 : 133 - 138 15. Jeon NJ , Noh JH , Kim YC , Yang WS , Ryu S , II Seok S ( 2014 ) Solvent engineering for high-performance inorganic-organic hybrid perovskite solar cells . Nature Mater 13 : 897 - 903 16. You J , Yang Y , Hong Z , Song T-B , Meng L , Liu Y , Jiang C , Zhou H , Chang WH , Li G , Yang Y ( 2014 ) Moisture assisted perovskite film growth for high performance solar cells . Appl Phys Lett 105 : 183902 17. Zhou H , Chen Q , Li G , Luo S , Song T , Duan H-S , Hong Z , You J , Liu Y , Yang Y ( 2014 ) Interface engineering of highly efficient perovskite solar cells . Science 345 : 542 - 546 18. Ahn N , Son D-Y , Jang I-H , Kang SM , Choi M , Park N-G ( 2015 ) Highly reproducible perovskite solar cells with average efficiency of 18.3 % and best efficiency of 19.7 % fabricated via Lewis base adduct of lead(II) iodide . J Am Chem Soc 137 : 8696 - 8699 19. Yang WS , Noh JH , Jeon NJ , Kim YC , Ryu S , Seo J , II Seok S ( 2015 ) Highperformance photovoltaic perovskite layers fabricated through intramolecular exchange . Science 348 : 6240 20. Chen Q , Zhou H , Hong Z , Luo S , Duan H-S , Wang H-H , Liu Y , Li G , Yang Y ( 2014 ) Planar heterojunction perovskite solar cells via vapor-assisted solution process . J Am Chem Soc 136 : 622 - 625 21. Xiao M , Huang F , Huang W , Dkhissi Y , Zhu Y , Etheridge J , Gray-Weale A , Bach U , Cheng Y-B, Spiccia L ( 2014 ) A fast deposition-crystallization procedure for highly efficient lead iodide perovskite thin-film solar cells . Angew Chem Int Ed 126 : 10056 - 10061 22. Xiao Z , Bi C , Shao Y , Dong Q , Wang Q , Yuan Y , Wang C , Gao Y , Huang J ( 2014 ) Efficient, high yield perovskite photovoltaic devices grown by interdiffusion of solution-processed precursor stacking layers . Energy Environ Sci 7 : 2619 - 2623 23. Liang P-W , Liao C-Y , Chueh C-C , Zuo F , Williams ST , Xin X-K , Lin J , Jen Alex K-Y ( 2014 ) Additive enhanced crystallization of solution-processed perovskite for highly efficient planar-heterojunction solar cells . Adv Mater 26 : 3748 - 3754 24. Song X , Wang W , Sun P , Ma W , Chen Z-K ( 2015 ) Additive to regulate the perovskite crystal film growth in planar heterojunction solar cells . Appl Phys Lett 106 : 864 25. Zhao Y , Zhu K ( 2014 ) CH3NH3Cl-assisted one-step solution growth of CH3NH3PbI3: structure, charge-carrier dynamics, and photovoltaic properties of perovskite solar cells . J Phys Chem C 118 : 9412 - 9418 26. Jeon Y-J , Lee S , Kang R , Kim J-E , Yeo J-S , Lee S-H , Kim S-S , Yun J-M , Kim D-Y ( 2014 ) Planar heterojunction perovskite solar cells with superior reproducibility . Sci Rep 4 : 6953 27. Eperon GE , Burlakov VM , Docampo P , Goriely A , Snaith HJ ( 2014 ) Morphological control for high performance, solution-processed planar heterojunction perovskite solar cells . Adv Funct Mater 24 : 151 - 157 28. Kang R , Kim J-E , Yeo J-S , Lee S , Jeon Y-J , Kim D-Y ( 2014 ) Optimized organometal halide perovskite planar hybrid solar cells via control of solvent evaporation rate . J Phys Chem C 118 : 26513 - 26520 29. Xiao Z , Dong Q , Bi C , Shao Y , Yuan Y , Huang J ( 2014 ) Solvent annealing of perovskite-induced crystal growth for photovoltaic-device efficiency enhancement . Adv Mater 26 : 6503 - 6509 30. Ren Z , Ng A , Shen Q , Gokkaya HC , Wang J , Yang L , Yiu W-K , Bai G , Djurišić AB , Leung WW , Hao J , Chan WK , Surya C ( 2014 ) Thermal assisted oxygen annealing for high efficiency planar CH3NH3PbI3 perovskite solar cells . Sci Rep 4 : 6752 31. Li Y , Cooper JK , Buonsanti R , Giannini C , Liu Y , Toma FM , Sharp ID ( 2015 ) Fabrication of planar heterojunction perovskite solar cells by controlled lowpressure vapor annealing . J Phys Chem Lett 6 : 493 - 499 32. Chen Q , Nicholas DM , Yang Y(M) , Song T-B , Chen C-C , Zhao H , Hong Z , Zhou H , Yang Y ( 2015 ) Under the spotlight: the organic-inorganic hybrid halide perovskite for optoelectronic applications . Nano Today 10 : 355 - 396 33. Kim J-S, Chung W-S , Kim K , Kim DY , Paeng K-J , Jo SM , Jang S-Y ( 2010 ) Performance optimization of polymer solar cells using electrostatically sprayed photoactive layers . Adv Funct Mater 20 : 3538 - 3546


This is a preview of a remote PDF: https://link.springer.com/content/pdf/10.1186%2Fs11671-016-1467-9.pdf

Qing-Yang Xu, Da-Xing Yuan, Hao-Ran Mu, Femi Igbari, Qiaoliang Bao, Liang-Sheng Liao. Efficiency Enhancement of Perovskite Solar Cells by Pumping Away the Solvent of Precursor Film Before Annealing, Nanoscale Research Letters, 2016, 248, DOI: 10.1186/s11671-016-1467-9