High White Light Photosensitivity of SnSe Nanoplate-Graphene Nanocomposites

Nanoscale Research Letters, Apr 2017

The multi-functional nanomaterial constructed with more than one type of materials has gained a great attention due to its promising application. Here, a high white light photodetector prototype established with two-dimensional material (2D) and 2D nanocomposites has been fabricated. The 2D-2D nanocomposites were synthesized with SnSe nanoplate and graphene. The device shows a linear I-V characterization behavior in the dark and the resistance dramatically decreases under the white light. Furthermore, the photosensitivity of the device is as large as 1110% with a rapid response time, which is much higher than pristine SnSe nanostructure reported. The results shown here may provide a valuable guidance to design and fabricate the photodetector based on the 2D-2D nanocomposites even beyond the SnSe nanoplate-graphene nanocomposites.

A PDF file should load here. If you do not see its contents the file may be temporarily unavailable at the journal website or you do not have a PDF plug-in installed and enabled in your browser.

Alternatively, you can download the file locally and open with any standalone PDF reader:

https://link.springer.com/content/pdf/10.1186%2Fs11671-017-2021-0.pdf

High White Light Photosensitivity of SnSe Nanoplate-Graphene Nanocomposites

Liu et al. Nanoscale Research Letters High White Light Photosensitivity of SnSe Nanoplate-Graphene Nanocomposites Jinyang Liu 0 1 2 3 Qingqing Huang 0 3 Kun Zhang 4 Yangyang Xu 0 1 2 3 Mingzhu Guo 0 3 Yongqiang Qian 0 3 Zhigao Huang 0 1 2 3 Fachun Lai 0 1 2 3 Limei Lin 0 1 2 3 0 College of Physics and Energy, Fujian Normal University , Fuzhou 350117 , People's Republic of China 1 Fujian Provincial Collaborative Innovation Center for Optoelectronic Semiconductors and Efficient Devices , Xiamen 361005 , People's Republic of China 2 Fujian Provincial Key Laboratory of Quantum Manipulation and New Energy Materials , Fuzhou 350117 , People's Republic of China 3 College of Physics and Energy, Fujian Normal University , Fuzhou 350117 , People's Republic of China 4 Center for Micro- and Nanoscale Research and Fabrication, University of Science and Technology of China , Hefei, Anhui 230026 , People's Republic of China The multi-functional nanomaterial constructed with more than one type of materials has gained a great attention due to its promising application. Here, a high white light photodetector prototype established with two-dimensional material (2D) and 2D nanocomposites has been fabricated. The 2D-2D nanocomposites were synthesized with SnSe nanoplate and graphene. The device shows a linear I-V characterization behavior in the dark and the resistance dramatically decreases under the white light. Furthermore, the photosensitivity of the device is as large as 1110% with a rapid response time, which is much higher than pristine SnSe nanostructure reported. The results shown here may provide a valuable guidance to design and fabricate the photodetector based on the 2D-2D nanocomposites even beyond the SnSe nanoplate-graphene nanocomposites. Photodetector; SnSe; Nanoplate-graphene; Nanocomposites; Photosensitivity - Background Atomically thin two-dimensional (2D) materials, including graphene [1?3], BN [4], Be2Se3 [5], MoS2 [6], GaSe [7], SnSe [8], and SnSe2 [9], have attracted great attention due to their unique properties distinguished from the bulks in the past decades. However, the single function of the material has become the bottleneck for their further application. As a result, building blocks in nanocomposites constructed with two or even more components have provided a new strategy. In particular, the nanocomposites constructed with the graphene have become a great interest. These nanocomposites not only preserve the favorable properties of graphene and the other components but also greatly enhance the intrinsic properties due to the synergetic effect between them. At present, three types of the composites based on graphene have been constructed: (i) 0D-2D nanocomposites, for example, ZnO NP-RGO [10], CdSe NP-RGO [11], PbS QD-graphene [12], and GeSi QD-graphene [12]; (ii) 1D-2D nanocomposites, for example, PbSe nanorod-graphene [13] and ZnO nanorod-graphene [14]; (iii) 2D-2D nanocomposites, for example, GaSe nanosheet-graphene [15], few-layer InSe-graphene [16], and CdSe nanosheet-graphene [17]. Among them, due to the larger interface region from the face-to-face contact comparing to the point-to-face contact in the 0D-2D nanocomposites and the line-toface contact in the 1D-2D nanocomposites, the 2D-2D nanocomposites are suggested to be the most promising materials in photodetector, photocatalysis, energy storage and conversion, sensor, and so on. In this report, the 2D-2D nanocomposites namely SnSe nanoplate-graphene nanocomposites were synthesized. As an important p-type semiconductor, SnSe has attracted intense attention in solar cells, photodetectors, and near-infrared optoelectronic devices due to its narrow band gap (~0.90 eV indirect and ~1.30 eV direct), earth-abundance, less toxicity, and chemical stability [18?20]. Then, a white light detector prototype based on the as-synthesized products was constructed after a series of characterization by XRD, SEM, and Raman. The device shows a linear I-V characterization behavior in the dark, and the resistance dramatically decreases under the white light. The photosensitivity of the device is as large as 1110% with a rapid response time. The ? The Author(s). 2017 Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. results shown here may provide a valuable instruction to design and fabricate photodetectors based on graphene and even extend to other 2D-2D nanocomposites. Methods Chemicals All chemical materials were of analytical grade and used as received without further purification. Tin (II) chloride dihydrate (SnCl2?2H2O; ?98%), polyvinylpyrrolidone (PVP; 99.0%), and benzyl alcohol (?98%) were purchased from Tianjing Fuchen Chemical Reagents Factory. Selenium dioxide (SeO2; 99.9%) were obtained from Chengdu Ai Keda Chemical Technology Co., Ltd. Graphite oxide (GO) was prepared through Hummers method [21]. Some common organic solvents (ethanol and so on) were of analytical grade and obtained from Sinopharm Chemical Reagent Co., Ltd. Synthesis of the SnSe Nanoplate-Graphene Nanocomposites In a typical synthesis of the SnSe nanoplate-graphene nanocomposite, SeO2 (0.8 mmol/L), SnCl2?2H2O (0.8 mmol/L) and poly (vinyl pyrrolidone) (PVP; 0.32 g/ mL), GO (0.075 g/mL) is added into benzyl alcohol (20 mL) at room temperature. The mixed solution was transferred into a three-neck round-bottom flask, sealed, and then degassed with pure N2 (99.99%) under magnetic stirring. Then the mixture was heated up to 200 ?C and allowed to be aged for another 12 h at this temperature in N2 atmosphere. Finally, the solution was cooled down to room temperature naturally, and the products were obtained by centrifugation at 10,000 rpm for 10 min to purify at least twice by re-suspending them into absolute alcohol. The products could then be well re-suspended in ethanol for further characterization. Characterization The powder X-ray diffraction pattern (XRD) is characterized by PANalytical X?Pert ProMPD (Cu K?, ? = 0.15418 nm). The UV-Vis-NIR was characterized by the Perkin Elmer Lambda 950. The scanning electron microscopy (SEM) was characterized by Hitachi SU-8010. Transmission electron microscopy (TEM) attached with selected area electron diffraction (SAED) was characterized by JEOL ARM-200F. The Raman spectroscopy was recorded at room temperature using HORIBA Jobin Yvon Evolution with laser excitation at 532 nm with power less than 5 mW. The interdigital gold electrode (the separation between them was 5 ?m) on the SiO2 substrate was fabricated by photolithography with lift-off technology. The electronic property was measured by Keithley 4200 semiconductor characterization systems. The SAN-EI ELECTRIC XES-40S1 Solar Simulator (100 mW/cm2) was used as the white light source. Results and Discussion Crystal Structure The powder X-ray diffraction (XRD) pattern is performed to elucidate the phase structure of the SnSe nanoplategraphene nanocomposites. As shown in Fig. 1, all of the diffraction peaks could be indexed to the orthorhombic SnSe structure with cell unit of a = 11.50 ?, b = 4.15 ?, and c = 4.44 ? (PDF #48-1244 Pnma(62)), which is consistent with the previous reports [8, 22]. It is worth-noting that the predominant peaks are (400), which indicate highly orientation of the SnSe nanoplates grown along (100) zone axis. Morphology and Raman Spectroscopy The as-synthesized products were then characterized by SEM and the typical results are shown in Fig. 2. The majority of the SnSe nanoplates were rectangular with a typical lateral size of 1?2 ?m, anchoring to the graphene sheet. The SnSe nanoplate-graphene nanocomposites are about ~10 ?m, which are consistent with the GO precursor. The graphene sheet is ambiguous in the lowmagnification SEM image due to the single atomic layer thickness; however, its wrinkle is observed in the highmagnification SEM image as shown in Fig. 2c, d. Through detailed examination of the samples, it can be found that the SnSe nanoplates have well size distribution and excellent dispersion on the graphene sheet. An interesting phenomenon was observed in the SEM characterization, only the SnSe nanoplates on the upper surface are able to be observed in the low accelerated voltage (1 kV) as shown in the Fig. 2c; however, in the high accelerated voltage (5 kV), the SnSe nanoplates on the bottom face can also be viewed clearly as shown in Fig. 2d. Consequently, it offers a novel method to distinguish the position of the SnSe nanoplates on graphene sheet, and it may be extended to characterize the similar Fig. 1 The XRD pattern of the SnSe-graphene nanostructure Fig. 2 a, b The low-magnification and high-magnification SEM image of SnSe nanoplate-graphene nanocomposites; c, d the SEM image of SnSe nanoplate-graphene nanocomposites characterized with the accelerated voltage of 1 and 5 kV, respectively structure. Therefore, it can be concluded that the SnSe nanoplates decorate on both sides of the graphene sheet. In order to obtain the detailed crystal structure and crystal quality of the as-synthesized products, the SnSe nanoplate-graphene nanocomposites were characterized by transmission electron microscopy (TEM), HRTEM, and the selected-area electron diffraction (SAED). As shown in Fig. 3a, the graphene lay flat on the TEM grids, and the SnSe nanoplates dispersed uniformly on the graphene sheet, which are consistent with the SEM results illustrated above. The SnSe nanoplates and graphene are relatively stable against the high energy electron beam irradiation in a TEM. In addition, the HRTEM image of the square area masked in Fig. 3a shows clear orthogonal lattice fringes with both lattice spacing of ~0.30 nm. The intersection angle of the lattice fringes is approximated 94? (Fig. 3b), which is in good agreement with the angle between the planes of (011) and (0-11) of the orthorhombic SnSe crystal structure [22]. Furthermore, the SAED data (Fig. 3c), taken from the individual SnSe nanoplate, exhibits a clear orthogonally symmetric spot pattern, indicating the single-crystal nature of the sample. Therefore, we can conclude that the assynthesized products show high quality, in which the SnSe nanoplate can be well anchored to and dispersed on the graphene sheet. Furthermore, the Raman spectroscopy was also performed to investigate the quality of the SnSe nanoplategraphene nanocomposites. As illustrated in Fig. 4a, four characteristic peaks at 69.1, 104.1, 154.4, and 181.0 cm?1 respectively are clearly observed, which are consistent with the previous report [8, 22]. The Raman peak at 104.1 cm?1 belongs to the B3g phonon mode originated from the rigid shear modes of a layer with respect to its neighbors in the c directions. It has the highest intensity, indicating the layer structure of the SnSe nanoplates, Fig. 3 a The low-magnification TEM image of the representative SnSe nanoplate-graphene nanocomposites; b, c the high-magnification TEM image and SAED pattern of the representative SnSe nanoplate of the rectangular of a, respectively Fig. 4 a, b The Raman spectrum of SnSe and graphene of the SnSe nanoplate-graphene nanocomposites which is consistent with the XRD results shown above. On the other hand, the D band at approximately 1349.8 cm?1 originated from the disorder and the G band at 1588.4 cm?1 coming from the in-phase vibration were all observed clearly (Fig. 4b), which are consistent with the intrinsic property of the reduced graphite oxide (RGO). All these results shown above indicate that the SnSe nanoplate-graphene nanocomposites have a high quality. Absorbance Spectrum The optical absorption behavior of the SnSe nanoplategraphene nanocomposites and GO dispersed in ethanol were studied by UV-Vis-NIR spectroscopy in the region of 400?1600 nm. As seen in Fig. 5, GO shows a strong absorption peak at 236 nm together with a weak shoulder peak at 301 nm, which is consistent with previous report [23, 24]. It is well known that the UV-vis spectrum of GO exhibits a dominant peak at 231 nm, corresponding to ? ? ?* transitions of aromatic C?C bonds, and a weak shoulder near 300 nm, attributing to ? ? ? transitions of C?O bonds [25]. On the other hand, the SnSe nanoplate-graphene nanocomposites Fig. 5 UV-vis absorption spectra of GO and the SnSe nanoplate-graphene nanocomposites show a good absorption from the near infrared spectrum (~1470 nm), visible-light to the ultraviolet-light region; and a strong absorption peak originated from RGO was observed at 265 nm, which may be generally regarded as the excitation of plasmon of graphitic structure. The results indicate that the SnSe nanoplates and RGO really existed in the hybrid. Due to their wide range absorption region, the as-synthesized products have attracted intense attention for application in solar cells, photodetectors, and near-infrared optoelectronic devices. Photo-Electronic Property of the Device In order to evaluate photo-electronic property of the SnSe nanoplate-graphene nanocomposites for the white light, the photodetector device prototype was fabricated as described in the inset of Fig. 6a. The white light photodetector device was fabricated by drop casting the SnSe nanoplate-graphene nanocomposite alcoholic solution onto an interdigital gold electrode on the SiO2 substrate. The electrode was fabricated by photolithography, and the separation between the adjacent fingers was 5 ?m. The white light response of the device was measured by Keithley 4200 apparatus under the periodical illumination of a sunlight simulator with a power density of 100 mW/cm2. The typical I-V characterization of the device is shown in Fig. 6a. The good linear behavior in the dark demonstrates the Ohmic contact between the Au electrode and hybrid material. However, it shows good linear behavior in positive voltage and non-linear behavior in the negative voltage under the white light. This phenomenon may come from the fact that one contact resistance is the ohmic contact and the other is the Schottky contact. The white light photoresponse current were also measured with a fixed bias of 15 V. The device shows an excellent performance as a white light photodetector, as demonstrated in Fig. 6b. First, the response to white light is reversible and stable, indicating the device is very robust. Second, the photosensitivity is much high. If we define the photosensitivity as the ratio of the current under the white light to that in the dark, it can be calculated to be as large as ~1110%. Fig. 6 a The typical I-V characterization of the photodetector device constructed with the SnSe nanoplate-graphene nanocomposites, the schematic and structural diagram of the photodetector shown in the left upside and right downside inset; b the photosensitivity of the photodetector device with the voltage of 15 V under the white light or not Third, the response is very quick. The response time of our device is only about 1 s and the recovery time can be less than 1 s. However, the performance of the devices fabricated with SnSe nanostructures were not very satisfactory in the past, for example, Zhao et al. [26] have grown the SnSe nanoplates by CVD and its photosensitivity is only about 140%; Li et al. [8] synthesized SnSe nanosheets through solution thermal reaction and constructed photodector device comprising the SnSe nanosheets and poly-(3-hexylthiophene) (P3HT) hybrid films and its highest photosensitivity is less than 200%. Therefore, the photosensitivity of our devices is at least five times larger than that previous reported [8, 26]. It may be understood that, upon exposure to white light, the electrons and hole carriers are first excited from the SnSe nanoplates and transferred to the RGO rapidly, considering the special energy band of SnSe nanoplates and RGO [11] and unique 2D-2D structure (as shown in the inset of Fig. 4a). On the other hand, the electrical conductivity of the SnSe is poor, while the electrical conductivity of the RGO is very good. Furthermore, as for the two atomically thin 2D materials, the SnSe nanoplates and RGO contain high specific surface area. And subsequently, the SnSe nanoplate-graphene nanocomposites possess larger interface region from the face-to-face contact between the SnSe nanoplates and graphene. Therefore, the RGO serving as the carrier collectors can transport the carriers to the electrodes more efficiently and rapidly. In this context, the interfacial design and control between the different components in the hybrid is very important, which is also the theme of the optoelectronic device and needed further understanding in the future. Conclusions The 2D-2D nanocomposites namely SnSe nanoplategraphene nanocomposites have been successfully synthesized and investigated. The photodetector device prototype of the as-synthesized products was fabricated and characterized carefully. The device shows a linear behavior in the dark and the resistance decreases sharply under the white light. Furthermore, the photosensitivity of the device is much larger than one order of magnitude with reversible and stable under a rapid response time, which is much better than previous reported. The high performance of the device may originate from the larger interface region from the face-to-face contact and special energy band of SnSe nanoplates and graphene. The results may hopefully be guidance to design and fabricate the photodetector based on the 2D-2D nanocomposites even beyond the SnSe nanoplate-graphene nanocomposites. Acknowledgements This work was financially supported by the Natural Science Foundation of China (No.11374052), the Natural Science Foundation of Fujian Province of China (2012J01256, 2013J01174, 2017J05003), Education Department of Fujian Province (JA15140) and the Science and Technology Project from Education Department of Fujian Province of China (JB13023). Authors? Contributions The idea of the study was conceived by JL, ZH, and FL; QH, MG, YQ do the experiments; KZ, LL, and YX carried out the optical microscopy, SEM, TEM and Raman spectroscopy. JL, ZH, FL, and LL interpreted the experiments and wrote this manuscript. All authors read and approved the final manuscript. 1. Geim AK , Novoselov KS ( 2007 ) The rise of graphene . Nat Mater 6 ( 3 ): 183 - 91 2. Liu JY , Huang ZG , Lai FC , Lin LM , Xu YY , Zuo CD et al ( 2015 ) Controllable growth of the graphene from millimeter-sized monolayer to multilayer on Cu by chemical vapor deposition . Nanoscale Res Lett 10 : 455 3. Liu Y , Xia Q , He J , Liu Z ( 2017 ) Direct observation of high photoresponsivity in pure graphene photodetectors . Nanoscale Res Lett 12 ( 1 ): 93 . doi:10.1186/ s11671- 017 - 1827 -0 4. Nag A , Raidongia K , Hembram KPSS , Datta R , Waghmare UV , Rao CNR ( 2010 ) Graphene analogues of BN: novel synthesis and properties . ACS Nano 4 ( 3 ): 1539 - 44 5. Zhuang A , Li JJ , Wang YC , Wen X , Lin Y , Xiang B et al ( 2014 ) Screwdislocation-driven bidirectional spiral growth of Bi2Se3 nanoplates . Angew Chem Int Edit 53 ( 25 ): 6425 - 9 6. Mak KF , Lee C , Hone J , Shan J , Heinz TF ( 2010 ) Atomically thin MoS2: a New direct-gap semiconductor . Phys Rev Lett 105 ( 13 ): 136805 7. Hu PA , Wen ZZ , Wang LF , Tan PH , Xiao K ( 2012 ) Synthesis of few-layer GaSe nanosheets for high performance photodetectors . ACS Nano 6 ( 7 ): 5988 - 94 8. Li L , Chen Z , Hu Y , Wang XW , Zhang T , Chen W et al ( 2013 ) Single-layer single-crystalline SnSe nanosheets . J Am Chem Soc 135 ( 4 ): 1213 - 6 9. Fang Z , Hao SH , Long LY , Fang H , Qiang TT , Song YX ( 2014 ) The enhanced photoelectrochemical response of SnSe2 nanosheets . Crystengcomm 16 ( 12 ): 2404 - 10 10. Liu JY , Yu XX , Zhang GH , Wu YK , Zhang K , Pan N et al ( 2013 ) High performance ultraviolet photodetector fabricated with ZnO nanoparticles-graphene hybrid structures . Chinese J Chem Phys 26 ( 2 ): 225 - 30 11. Lin Y , Zhang K , Chen WF , Liu YD , Geng ZG , Zeng J et al ( 2010 ) Dramatically enhanced photoresponse of reduced graphene oxide with linker-free anchored CdSe nanoparticles . ACS Nano 4 ( 6 ): 3033 - 8 12. Konstantatos G , Badioli M , Gaudreau L , Osmond J , Bernechea M , de Arquer FPG et al ( 2012 ) Hybrid graphene-quantum dot phototransistors with ultrahigh gain . Nat Nanotechnol 7 ( 6 ): 363 - 8 13. Talebi H , Dolatyari M , Rostami G , Manzuri A , Mahmudi M , Rostami A ( 2015 ) Fabrication of fast mid-infrared range photodetector based on hybrid graphene-PbSe nanorods . Appl Opt 54 ( 20 ): 6386 - 90 14. Dang VQ , Trung TQ , Kim DI , Duy LT , Hwang BU , Lee DW et al ( 2015 ) Ultrahigh responsivity in graphene-ZnO nanorod hybrid UV photodetector . Small 11 ( 25 ): 3054 - 65 15. Lu RT , Liu JW , Luo HF , Chikan V , Wu JZ ( 2016 ) Graphene/GaSe-nanosheet hybrid: towards high gain and fast photoresponse . Sci Rep 6 : 19161 16. Chen ZS , Biscaras J , Shukla A ( 2015 ) A high performance graphene/fewlayer InSe photo-detector . Nanoscale 7 ( 14 ): 5981 - 6 17. Robin A , Lhuillier E , Xu XZ , Ithurria S , Aubin H , Ouerghi A et al ( 2016 ) Engineering the charge transfer in all 2D graphene-nanoplatelets heterostructure photodetectors . Sci Rep 6 : 24909 18. Franzman MA , Schlenker CW , Thompson ME , Brutchey RL ( 2010 ) Solutionphase synthesis of SnSe nanocrystals for use in solar cells . J Am Chem Soc 132(12):4060 19. Baumgardner WJ , Choi JJ , Lim YF , Hanrath T ( 2010 ) SnSe nanocrystals: synthesis, structure, optical properties, and surface chemistry . J Am Chem Soc 132 ( 28 ): 9519 - 21 20. Liu S , Guo XY , Li MR , Zhang WH , Liu XY , Li C ( 2011 ) Solution-phase synthesis and characterization of single-crystalline SnSe nanowires . Angew Chem Int Edit 50 ( 50 ): 12050 - 3 21. Williams G , Seger B , Kamat PV ( 2008 ) TiO2-graphene nanocomposites. UV-assisted photocatalytic reduction of graphene oxide . ACS Nano 2 ( 7 ): 1487 - 91 22. Liu JY , Huang QQ , Qian YQ , Huang ZG , Lai FC , Lin LM et al ( 2016 ) Screw dislocation-driven growth of the layered spiral-type SnSe nanoplates . Cryst Growth Des 16 ( 4 ): 2052 - 6 23. Zhu Y , James DK , Tour JM ( 2012 ) New routes to graphene, graphene oxide and their related applications . Adv Mater 24 ( 36 ): 4924 - 55 . doi:10.1002/adma. 201202321 24. Li D , Muller MB , Gilje S , Kaner RB , Wallace GG ( 2008 ) Processable aqueous dispersions of graphene nanosheets . Nat Nanotechnol 3 ( 2 ): 101 - 5 . doi:10.1038/nnano.2007.451 25. Paredes JI , Villar-Rodil S , Martinez-Alonso A , Tascon JMD ( 2008 ) Graphene oxide dispersions in organic solvents . Langmuir 24 ( 19 ): 10560 - 4 . doi:10.1021/La801744a 26. Zhao S , Wang H , Zhou Y , Liao L , Jiang Y , Yang X et al ( 2015 ) Controlled synthesis of single-crystal SnSe nanoplates . Nano Res 8 ( 1 ): 288 - 95 . doi:10.1007/s12274- 014 - 0676 -8


This is a preview of a remote PDF: https://link.springer.com/content/pdf/10.1186%2Fs11671-017-2021-0.pdf

High White Light Photosensitivity of SnSe Nanoplate-Graphene Nanocomposites, Nanoscale Research Letters, 2017, DOI: 10.1186/s11671-017-2021-0