Photoexcited Properties of Tin Sulfide Nanosheet-Decorated ZnO Nanorod Heterostructures

Nanoscale Research Letters, Apr 2017

In this study, ZnO–Sn2S3 core–shell nanorod heterostructures were synthesized by sputtering Sn2S3 shell layers onto ZnO rods. The Sn2S3 shell layers consisted of sheet-like crystallites. A structural analysis revealed that the ZnO–Sn2S3 core–shell nanorod heterostructures were highly crystalline. In comparison with ZnO nanorods, the ZnO–Sn2S3 nanorods exhibited a broadened optical absorption edge that extended to the visible light region. The ZnO–Sn2S3 nanorods exhibited substantial visible photodegradation efficiency of methylene blue organic dyes and high photoelectrochemical performance under light illumination. The unique three-dimensional sheet-like Sn2S3 crystallites resulted in the high light-harvesting efficiency of the nanorod heterostructures. Moreover, the efficient spatial separation of photoexcited carriers, attributable to the band alignment between ZnO and Sn2S3, accounted for the superior photocatalytic and photoelectrochemical properties of the ZnO–Sn2S3 core–shell nanorod heterostructures.

A PDF file should load here. If you do not see its contents the file may be temporarily unavailable at the journal website or you do not have a PDF plug-in installed and enabled in your browser.

Alternatively, you can download the file locally and open with any standalone PDF reader:

http://link.springer.com/content/pdf/10.1186%2Fs11671-017-2022-z.pdf

Photoexcited Properties of Tin Sulfide Nanosheet-Decorated ZnO Nanorod Heterostructures

Liang et al. Nanoscale Research Letters Photoexcited Properties of Tin Sulfide Nanosheet-Decorated ZnO Nanorod Heterostructures Yuan-Chang Liang 0 Tsai-Wen Lung 0 Nian-Cih Xu 0 0 Institute of Materials Engineering, National Taiwan Ocean University , Keelung 20224 , Taiwan In this study, ZnO-Sn2S3 core-shell nanorod heterostructures were synthesized by sputtering Sn2S3 shell layers onto ZnO rods. The Sn2S3 shell layers consisted of sheet-like crystallites. A structural analysis revealed that the ZnO-Sn2S3 core-shell nanorod heterostructures were highly crystalline. In comparison with ZnO nanorods, the ZnO-Sn2S3 nanorods exhibited a broadened optical absorption edge that extended to the visible light region. The ZnO-Sn2S3 nanorods exhibited substantial visible photodegradation efficiency of methylene blue organic dyes and high photoelectrochemical performance under light illumination. The unique three-dimensional sheet-like Sn2S3 crystallites resulted in the high light-harvesting efficiency of the nanorod heterostructures. Moreover, the efficient spatial separation of photoexcited carriers, attributable to the band alignment between ZnO and Sn2S3, accounted for the superior photocatalytic and photoelectrochemical properties of the ZnO-Sn2S3 core-shell nanorod heterostructures. Morphology; Surface; Sulfide; Sputtering; Heterostructure - Background A considerable number of researchers have examined the solar light-harvesting characteristics of oxide semiconductors to solve energy and environmental problems. Because of their high specific surface area values, nanostructured oxide semiconductors can be applied with high efficiency in various photoexcited devices [1?3]. Among various oxides, ZnO is a promising semiconductor material with a wide bandgap of approximately 3.3 eV, a large exciton binding energy of 60 meV, stable chemical properties, high electrochemical activity, and low cost. Thus, researchers have focused on the utilization of one-dimensional ZnO nanostructures in abundant photovoltaic, optoelectronic, and energy-related device applications [4?6]. However, the wide bandgap of ZnO significantly restricts its use under solar light because only a limited percentage of solar radiation is within the ultraviolet (UV) range. Several methods, such as crystal defect density control and chemical composition modification of ZnO nanostructures, have been adopted to improve the solar light-harvesting efficiency of ZnO [7, 8] and have produced limited improvements of the light-harvesting efficiency of ZnO. The efficiency levels of photoexcited devices made from ZnO nanostructures under solar light irradiation still require substantial improvement. Improvement of the light-harvesting efficiency of onedimensional ZnO oxides and reduction of the recombination rate of photoexcited carriers in these oxides are crucial to produce various highly efficient photoexcited nanodevices from ZnO nanostructures. Research has proven the construction of one-dimensional ZnO-based heterostructures to be a promising approach to obtain ZnO nanostructures with relatively high photoactivated performance; by contrast, devices with single ZnO components are less promising. Recent studies have reported that one-dimensional semiconductor composites are of potential for photocatalytic applications [9?11]. Moreover, ZnO nanostructures coupled with narrow-bandgap materials, such as CdS and CdSe, exhibit enhanced photoactivated performance levels [12, 13]. Thus, it is highly desirable to design and fabricate one-dimensional ZnO-based heterostructures through appropriate band alignment and coupling with narrow-bandgap semiconductors for applications in various photoexcited devices. The metal sulfides of semiconductors usually exhibit ? The Author(s). 2017 Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. superior light absorption in the visible region and exhibit absorption edges within the near-infrared region, which facilitate their response to the visible light of the solar spectrum, thus improving light-harvesting efficiency. Moreover, metal sulfides such as SnS, SnS2, and Sn2S3 have been used for visible light-driven photocatalytic reactions [14?16]. Among various metal sulfides, Sn2S3 has a narrow bandgap of approximately 1.1?2.05 eV and exhibits superior optical properties [16?18]. It is nonpoisonous, chemically stable, and inexpensive; therefore, it is a potential visible light sensitizer for photocatalytic, photovoltaic, and photoelectric devices. However, few studies have focused on coupling Sn2S3 with ZnO to form low-dimensional heterostructures. In the present study, ZnO?Sn2S3 core?shell heterostructures with special three-dimensional shell architecture were synthesized by sputtering Sn2S3 crystallites onto the surfaces of ZnO nanorods; the superior photoactivated properties of the ZnO?Sn2S3 core?shell heterostructures were investigated and were found to be highly correlated with the microstructures of the heterostructures. Methods In this study, ZnO-based core?shell nanorod heterostructures with the Sn2S3 shell layer (ZnO?Sn2S3 nanorods) were synthesized through a combinational methodology of hydrothermal and sputtering. Hydrothermally synthesized high-density ZnO nanorods were used as templates for growing the ZnO?Sn2S3 nanorod heterostructures. Detailed experiments on the hydrothermal synthesis of ZnO nanorods have been described elsewhere [19]. The Sn2S3 shell layers were fabricated by using radio frequency magnetron sputtering. The target sputtering power was fixed at 40 W in pure Ar ambient. The thin-film growth temperature of the Sn2S3 thin films was maintained at 250 ?C. During thin-film sputtering deposition, the gas pressures of the Sn2S3 shell layers were fixed at 10 mTorr. Sample crystal structures were investigated by X-ray diffraction (XRD; Bruker D2 PHASER) using Cu K? radiation. The surface morphology of the samples was investigated by scanning electron microscopy (SEM; Hitachi S-4800). The microstructures of the rod samples were characterized by high-resolution transmission electron microscopy (HRTEM; Philips Tecnai F20 G2). The optical absorption spectra of the samples were recorded in the wavelength range of 300?800 nm by using UV?Vis spectrophotometer (Jasco V750). Room temperaturedependent photoluminescence (PL; Horiba HR800) spectra were obtained using the 325 nm line of a He?Cd laser. The photocatalytic activities of as-prepared samples were investigated by measuring the photodegradation rate of methylene blue (MB; 10?6 M) as organic dyes under solar light irradiation. Prior to illumination, MB aqueous solution containing different samples were continuously stirred in the dark for 30 min to achieve adsorption/desorption equilibrium between the catalysts. After reaction, the solution was analyzed by measuring the absorption intensity of the main peak at approximately 663 nm by UV?Vis spectrophotometer. The photoelectrochemical (PEC) properties were measured in a convenient three electrodes electrochemical system (SP-50 Potentiostat/Galvanostat). The pure ZnO and ZnO?Sn2S3 nanorod heterostructures grown on the conductive F-doped SnO2 glasses were used as the working electrode, a platinum wire as the counter electrode, and an Ag/AgCl as the reference electrode. Aqueous solution containing 0.25 M of Na2S and 0.35 M of Na2SO3 was utilized as the electrolyte in an electrochemical system [20]. The intensity of illumination at the sample position was fixed to be approximately 50 mW cm?2 in this study. Results and Discussion Figure 1a, b illustrates the morphology of the ZnO nanorods. The surfaces of the ZnO nanorods were smooth with a hexagonal crystal feature. Figure 1c, d depicts the morphologies of the ZnO?Sn2S3 core?shell nanorods. SEM micrographs demonstrated that the hexagonal ZnO nanorods became circular, and the surfaces of the ZnO?Sn2S3 nanorods exhibited undualations and a visible sheet-like crystal texture. The sheet-like crystallites on the surfaces of the ZnO?Sn2S3 core?shell nanorods had sharp peripheries and were homogeneously distributed on the ZnO nanorods. The SEM micrographs showed that the surfaces of the ZnO?Sn2S3 nanorods were rougher than those of the ZnO nanorods, thus the ZnO?Sn2S3 nanorods had larger surface areas. Figure 2 shows the XRD pattern of the ZnO?Sn2S3 nanorods. The XRD pattern displays an intense and sharp Bragg reflection centered at approximately 34.4?, which is ascribed to the (002) crystallographic plane of the hexagonal ZnO nanorods (JCPDS no. 05-0664). The ZnO nanorods were highly crystalline, and the grains were oriented along the c-axis. Moreover, the XRD pattern displays three other sharp Bragg reflections with relatively low intensities centered at approximately 26.5?, 30.8?, and 31.9?. These Bragg reflections originated from the (111), (310), and (211) crystallographic planes of the orthorhombic Sn2S3 (JCPDS no. 14-0619). The XRD pattern indicates that the as-deposited Sn2S3 shell layer was polycrystalline, and the as-synthesized ZnO?Sn2S3 nanorods were highly crystalline. Figure 3a shows a low-magnification TEM image of the ZnO?Sn2S3 core?shell nanorod. The TEM image reveals that the ZnO?Sn2S3 nanorod had sheet-like surface morphology, which was considerably rough. Figure 3b shows the selected area electron diffraction (SAED) Fig. 1 a Low-magnification SEM micrograph of ZnO nanorods. b High-magnification SEM micrograph of ZnO nanorods. c Low-magnification SEM micrograph of ZnO?Sn2S3 nanorods. d High-magnification SEM micrograph of ZnO?Sn2S3 nanorods pattern detected from the nanorod. The SAED pattern exhibits one set of diffraction spots that can be indexed into the [010] zone axis of the hexagonal ZnO nanorod and several diffraction rings that can be indexed into Sn2S3 (111) and (310) crystallographic planes. The SAED pattern reveals that the ZnO?Sn2S3 core?shell nanorod exhibited appropriate crystalline phases and that the crystallographic planes were in close agreement with the XRD results. Figure 3c, d presents HRTEM images taken from the outer regions of the ZnO?Sn2S3 nanorod. The HRTEM images reveal clear and long-range ordered lattice fringes that were regionally distributed. The lattice fringes with intervals of approximately 0.261 nm in the inner region corresponded to hexagonal ZnO (002). The Fig. 2 XRD pattern of ZnO?Sn2S3 nanorods lattice fringes with intervals of approximately 0.289 and 0.335 nm in the outer region matched the spacing distances of Sn2S3 (310) and (111) crystallographic planes, respectively. The TEM analyses reveal a highly crystalline ZnO?Sn2S3 core?shell nanorod with a strongly undulated surface. The optical absorption edges of the pure ZnO and ZnO?Sn2S3 rods were evaluated by measuring the diffuse reflectance spectra of the samples and by converting these spectra into absorption coefficient spectra with the Kubelka?Munk function [21, 22]. Figure 4a displays the Kubelka?Munk conversion spectra of the pure ZnO and ZnO?Sn2S3 nanorods. Typically, ZnO has a wide-bandgap value in the UV light region. Moreover, Sn2S3 with the same effective shell thickness showed a bandgap value in the visible light region as exhibited in the inset of Fig. 4a; the bandgap value can be estimated from the absorbance spectra by using the Tauc plot and the bandgap is approximately 1.83 eV. In this study, in comparison with the pure ZnO nanorods, the ZnO?Sn2S3 nanorods exhibited a broadened optical absorption edge that extended to the visible light region. The ZnO?Sn2S3 nanorods exhibited visible light-sensitive features. The broader absorption spectrum and lower absorption edge energy indicated that the ZnO?Sn2S3 nanorod heterostructures had superior optical absorption capability under light illumination. It has been reported that the construction of a heterostructure by coupling with the visible light sensitizers similarly extended the optical absorption edge of the wide-bandgap oxides in other material systems (i.e., ZnO?CdS, TiO2?Ag2S, and SnO2?Fe2O3) [23?25]. Figure 4b displays the roomtemperature PL spectra of the ZnO and ZnO?Sn2S3 Fig. 3 TEM analyses of the ZnO?Sn2S3 nanorod heterostructure. a Low-magnification TEM image of the ZnO?Sn2S3 nanorod. b SAED pattern of the nanorod. c, d HRTEM images taken from the local regions of the nanorod nanorods. A UV emission band centered at approximately 378 nm can be ascribed to the near-band edge emission of the ZnO rods [19]. Furthermore, the ZnO and ZnO?Sn2S3 nanorods exhibited broad emission bands centered at approximately 560 and 530 nm, respectively. These broad visible light emission bands are referred to as deep-level or trap-state emission bands and might be associated with structural defects arising from the oxygen vacancies of the ZnO core and the shallow trap caused by the surface states of the sulfide shell layer [19, 26]. In comparison with the broad emission bands, the intensity of the near-band edge emission from ZnO was markedly quenched when the Sn2S3 crystallites were sputtered onto the surfaces of the ZnO nanorods. This finding indicated that the recombination of the photogenerated charge carrier was considerably inhibited in the ZnO?Sn2S3 heterostructures. The photocatalytic activities of the nanorod samples were evaluated by photodegradation of MB under solar light irradiation with various durations. Figure 5a, b illustrates the time course-dependent absorbance spectra of the ZnO and ZnO?Sn2S3 nanorods under solar light illumination. The visible and intense peaks of the absorption spectra at approximately 663 nm can be ascribed to monomeric MB. The intensity of the absorbance peak centered at approximately 663 nm for the MB solution containing the ZnO and ZnO? Sn2S3 nanorods decreased with increased reaction duration. The photodegradation size was defined as (C/Co), where Co is the concentration of aqueous MB without irradiation after dark adsorption equilibrium, and C is the concentration of aqueous MB corresponding to a given light irradiation duration [27]. For a comparison, the absorbance spectra of the MB solution containing ZnO?Sn2S3 nanorods under visible light irradiation with various durations were also shown in Fig. 5c. An ultraviolet light filter was used during the photodegradation test. Figure 5d shows that under light illumination, the photodegradation size of MB increased with reaction duration when ZnO nanorods were used as catalysts. In comparison with the ZnO nanorods, the ZnO?Sn2S3 nanorods photodegraded MB organic dyes with substantially higher efficiency under the same reaction conditions. The superior photocatalytic performance of the ZnO? Sn2S3 core?shell structure is attributable to the band relation of the heterostructure. Notably, Sn2S3 is a narrow-bandgap semiconductor with a reported electron affinity of approximately 3.56 eV [17], whereas ZnO is an n-type wide-bandgap semiconductor with a reported electron affinity of 4.35 eV [28]. These data may provide reliable references to approximately estimate the relative band edge positions of the two semiconductors. The contact of ZnO and Sn2S3 forms a type II band alignment structure. When the ZnO? Fig. 4 a Optical absorbance spectra of the ZnO and ZnO?Sn2S3 nanorods. The inset shows the optical absorbance spectrum of the Sn2S3 film. b PL spectra of the ZnO and ZnO?Sn2S3 nanorods Sn2S3 heterojunction is formed, electrons tend to flow from Sn2S3 to ZnO, resulting in electron accumulation on the ZnO side [29]. Figure 5e illustrates the possible band alignment of the ZnO?Sn2S3 heterostructure. As shown in Fig. 5e, when the ZnO?Sn2S3 nanorods are irradiated by solar light, the ZnO cores of the heterostructures respond to UV light because of the wide bandgap of ZnO, and numerous photoexcited electrons and holes are generated. Simultaneously, photoexcited electron?holes are also generated in Sn2S3 shells under light irradiation. The photoexcited electrons in the Sn2S3 shell layers tend to be transferred from the conduction band of Sn2S3 to the conduction band of ZnO through the interface, whereas the photoexcited holes in the ZnO are transferred to the valence band of Sn2S3. A predictable photoexcited charge transfer between ZnO and Sn2S3 can be noted. A previous study demonstrated that efficient spatial charge separation prolongs the lifetime of photoexcited charges in a semiconductor composite system [22]. In that study, a higher-than-usual number of photoexcited electrons near the surfaces of ZnO rods were captured by O2 molecules to yield superoxide radical anions (O?2?) and hydrogen peroxide (H2O2); subsequently, the reaction of O?2? with H2O2 generated ?OH. Moreover, a higher-than-usual number of photoexcited holes near the shell surfaces of the rod heterostructures oxidized H2O molecules to produce hydroxyl radicals (?OH), which were strong oxidizing agents that effectively decomposed MB [22]. The band configuration of the ZnO?Sn2S3 heterostructure reduces the electron?hole recombination probability; this is similar to the ZnO?In2S3 rod heterostructure system, which also exhibits higher photocatalytic properties than those of its ZnO counterpart [30]. Furthermore, the higher surface area of the ZnO?Sn2S3 nanorods exposed to organic dyes can provide more active catalytic sites to increase photocatalytic activity [31]. The aforementioned factors explain the markedly improved photocatalytic performance of the ZnO nanorods coated with the Sn2S3 shell layers in this study. To confirm the recycling ability and long-term chemical stability of the ZnO?Sn2S3 nanorods, a photodegradation test of MB solution containing ZnO?Sn2S3 nanorods under light irradiation was repeated three times as exhibited in Fig. 5f. No significant variation was found in the photodegradation efficiency of the ZnO?Sn2S3 nanorods in different test runs. It has been shown that the reaction of the photogenerated holes with the surface oxygen of ZnO is the main reason for the photocorrosion process of ZnO. The suppression of the reaction between the photogenerated holes and surface oxygen is beneficial to stabilize the photoactivity of ZnO [32]. The high photoactivity and photostability for the ZnO?Sn2S3 nanorods in this study is associated with the ZnO nanorods capsulated by sheetlike Sn2S3 crystallites. This engendered more MB molecules could be adsorbed, which consumed more holes photoexcited from ZnO core and competed with the dissolution process of ZnO. This finding demonstrates that these ZnO?Sn2S3 nanorods are stable and reusable catalysts for photodegrading MB organic dyes. Figure 6a shows the photocurrent density vs. the potential curves of the ZnO and ZnO?Sn2S3 nanorods with and without light illumination. Under light irradiation, the measured photocurrent densities of the ZnO and ZnO?Sn2S3 nanorods were approximately 0.32 and 0.84 mA cm?2 at 0.5 V, respectively. The ZnO nanorod sample yielded relatively low photocurrent under light illumination. However, the sequential combination of the Sn2S3 shell layers onto the surfaces of the ZnO nanorods significantly enhanced the photocurrent density. These results confirmed that the ZnO?Sn2S3 Fig. 5 Intensity variation of absorbance spectra of MB solution vs. degradation duration containing various nanorods samples under light illumination. a Pure ZnO nanorods under solar light illumination. b ZnO?Sn2S3 nanorods under solar light illumination. c ZnO?Sn2S3 nanorods under visible light illumination. d C/Co vs. irradiation time curves for MB solution with various nanorod samples under light illumination. e A schematic of band alignment and charges transfer of the ZnO?Sn2S3 heterostructure under light illumination. f Recycled performance (three test runs) in the presence of ZnO?Sn2S3 nanorods for photodegradation of MB dyes nanorods exhibited efficient visible light absorption ability and excellent interfacial charge transformation. Figure 6b displays the photocurrent responses of the ZnO and ZnO?Sn2S3 nanorods at an applied potential of 0.5 V. The ZnO?Sn2S3 nanorods exhibited steady and highly repeatable photocurrent responses during on?off cycles of light illumination. Notably, photoexcited electrons in the Sn2S3 are injected into ZnO because of the band alignment of the heterostructure, as discussed earlier in the present text. This is attributed to the type II band alignment between the ZnO and Sn2S3; the effective photoexcited charge separation has been widely reported in other heterostructure systems [33, 34]. The aligned ZnO nanorods provide a conduction path, and numerous photoexcited electrons are transferred from Sn2S3 and ZnO to the Fdoped SnO2 electrode and are then finally transferred to the platinum electrode. After the photogenerated carriers are transferred rapidly in the PEC system, the electrons travel through F-doped SnO2 to the platinum electrode and react with the electrolyte, yielding a reduction reaction, whereas the holes in the valence band of Sn2S3 react with the electrolyte, yielding an oxidation reaction [34]. Consequently, the ZnO nanorods coated with the Sn2S3 shell layers exhibit excellent PEC activity compared with that of pure ZnO rods. In this study, the superior PEC performance of the ZnO?Sn2S3 nanorod heterostructures is attributable to the increased contact area between the nanorods and adsorbed electrolyte molecules resulting from the unique three-dimensional sheet-like Sn2S3 layers of the ZnO?Sn2S3 rod heterostructures. Furthermore, Sn2S3 exhibits superior optical absorption ability, providing high visible light-harvesting efficiency. These factors account for the superior PEC activity of the ZnO?Sn2S3 nanorods in this study. Conclusions In this study, ZnO?Sn2S3 core?shell nanorod heterostructures were synthesized by sputtering Sn2S3 shell layers onto hydrothermally derived ZnO nanorods. The microstructural analyses revealed that the surfaces of the ZnO?Sn2S3 nanorod heterostructures had a sheet-like texture, and the nanorod heterostructures were highly crystalline. The optical absorption spectra analysis revealed that the ZnO?Sn2S3 nanorods exhibited a visible light-sensitive feature. Compared with ZnO nanorods, the ZnO?Sn2S3 nanorods exhibited enhanced photodegradation efficiency of MB organic dyes and improved PEC performance under light illumination. The unique sheet-like shell structures resulted in a high surface area of the nanorod Fig. 6 a Current density vs. potential curves for various nanorod samples with and without light illumination. b Cyclic current density vs. time curves for various nanorod samples under chopped light illumination heterostructures. Moreover, the suitable band alignment between the ZnO and Sn2S3 decreased the recombination efficiency of the light-excited carriers in the composite nanorods. These factors explain the superior photocatalytic and PEC properties of the ZnO?Sn2S3 nanorod heterostructures. Authors? Contributions YCL designed the experiments and drafted the manuscript. TWL and NCX carried out the sample preparations, characterization tests, and data analyses. All authors read and approved the final manuscript. 1. Li L , Dai H , Feng L , Luo D , Wang S , Sun X ( 2015 ) Enhance photoelectrochemical hydrogen-generation activity and stability of TiO2 nanorod arrays sensitized by PbS and CdS quantum dots under UV-visible light . Nanoscale Res Lett 10 : 418 2. Liang YC , Liu SL , Hsia HY ( 2015 ) Physical synthesis methodology and enhanced gas sensing and photoelectrochemical performance of 1D serrated zinc oxide-zinc ferrite nanocomposites . Nanoscale Res Lett 10 : 350 3. Liang YC , Lin TY , Lee CM ( 2015 ) Crystal growth and shell layer crystal feature-dependent sensing and photoactivity performance of zinc oxide-indium oxide core-shell nanorod heterostructures . CrystEngComm 17 : 7948 - 7955 4. Liang YC , Liao WK ( 2014 ) Annealing induced solid-state structure dependent performance of ultraviolet photodetectors made from binary oxide-based nanocomposites . RSC Adv 4 : 19482 - 19487 5. Chu S , Li D , Chang PC , Lu JG ( 2010 ) Flexible dye-sensitized solar cell based on vertical ZnO nanowire arrays . Nanoscale Res Lett 6:38 6. Roza L , Rahman MYA , Umar AA , Salleh MM ( 2015 ) Direct growth of oriented ZnO nanotubes by self-selective etching at lower temperature for photo-electrochemical (PEC) solar cell application . J Alloy Compd 618 : 153 - 158 7. Wang J , Xia Y , Dong Y , Chen R , Xiang L , Komarneni S ( 2016 ) Defect-rich ZnO nanosheets of high surface area as an efficient visible-light photocatalyst . Appl Catal B 192 : 8 - 16 8. Omidi A , Habibi-Yangjeh A , Pirhashemi M ( 2013 ) Application of ultrasonic irradiation method for preparation of ZnO nanostructures doped with Sb+3 ions as a highly efficient photocatalyst . Appl Surf Sci 276 : 468 - 475 9. Zhang N , Xie S , Weng B , Xu YJ ( 2016 ) Vertically aligned ZnO-Au@CdS core-shell nanorod arrays as an all-solid-state vectorial Z-scheme system for photocatalytic application . J Mater Chem A 4 : 18804 - 18814 10. Liu S , Han C , Tang ZR , Xu YJ ( 2016 ) Heterostructured semiconductor nanowire arrays for artificial photosynthesis . Mater Horiz 3 : 270 - 282 11. Bo W , Liu S , Tang ZR , Xu YJ ( 2014 ) One-dimensional nanostructure based materials for versatile photocatalytic applications . RSC Adv 4 : 12685 - 12700 12. Zhu YF , Fan DH , Zhou GH , Liu L ( 2014 ) A suitable chemical conversion route to synthesize ZnO/CdS core/shell heterostructures for photovoltaic applications . Ceram Int 40 : 3353 - 3359 13. Wub Y , Xua F , Guob D , Gaoa Z , Wua D , Jiang K ( 2013 ) Synthesis of ZnO/ CdSe hierarchical heterostructure with improved visible photocatalytic efficiency . Appl Surf Sci 274 : 39 - 44 14. Zhang G , Fu Z , Wang Y , Wang H ( 2015 ) Facile synthesis of hierarchical SnS nanostructures and their visible light photocatalytic properties . Adv Powder Technol 26 : 1183 - 1190 15. Luo J , Zhou X , Zhang J , Du Z ( 2015 ) Fabrication and characterization of Ag2CO3/SnS2 composites with enhanced visible-light photocatalytic activity for the degradation of organic pollutants . RSC Adv 5 : 86705 - 86712 16. Wang Z , Wang Z , Wang D , Chen M ( 2016 ) Ultra-small Sn2S3 porous nano-particles: an excellent photo-catalyst in the reduction of aqueous Cr(VI) under visible light irradiation . RSC Adv 6 : 12286 - 12289 17. Whittles TJ , Burton LA , Skelton JM , Walsh A , Veal TD , Dhanak VR ( 2016 ) Band alignments, valence bands, and core levels in the tin sulfides SnS, SnS2, and Sn2S3: experiment and theory . Chem Mater 28 : 3718 - 3726 18. Sanchez-Juarez A , Ort??z A ( 2002 ) Effects of precursor concentration on the optical and electrical properties of SnXSY thin films prepared by plasma-enhanced chemical vapour deposition . Semicond Sci Technol 17 : 931 - 937 19. Liang YC , Liu SL ( 2015 ) Structure-dependent gas detection ability of clustered ZnS crystallites with heterostructure and tube-like architecture . Acta Mater 88 : 245 - 251 20. Tang Y , Traveerungroj P , Tan HL , Wang P , Amal R , Ng YH ( 2015 ) Scaffolding an ultrathin CdS layer on a ZnO nanorod array using pulsed electrodeposition for improved photocharge transport under visible light illumination . J Mater Chem A 3 : 19582 - 19587 21. Chen Z , Zhang N , Xu YJ ( 2013 ) Synthesis of graphene-ZnO nanorod nanocomposites with improved photoactivity and anti-photocorrosion . Cryst Eng Comm 15 : 3022 - 3030 22. Liang YC , Lung TW ( 2016 ) Growth of hydrothermally derived CdS-based nanostructures with various crystal features and photoactivated properties . Nanoscale Res Lett 11 : 264 23. Zou Z , Xie C , Zhang S , Yang C , Zhang G , Yang L ( 2013 ) CdS/ZnO nanocomposite film and its enhanced photoelectric response to UV and visible lights at low bias . Sens Actuators B 188 : 1158 - 1166 24. Jana S , Mondal A ( 2014 ) Fabrication of SnO2/?-Fe2O3, SnO2/?-Fe2O3-PB heterostructure thin films: enhanced photodegradation and peroxide sensing . ACS Appl Mater Interfaces 6 : 15832 - 15840 25. Ong WL , Lim YF , Ong JLT , Ho GW ( 2015 ) Room temperature sequential ionic deposition (SID) of Ag2S nanoparticles on TiO2 hierarchical spheres for enhanced catalytic efficiency . J Mater Chem A 3 : 6509 - 6516 26. Huang L , Yang J , Wang X , Han J , Han H , Li C ( 2013 ) Effects of surface modification on photocatalytic activity of CdS nanocrystals studied by photoluminescence spectroscopy . Phys Chem Chem Phys 15 : 553 - 560 27. Liang YC , Chung CC , Lin TY , Cheng YR ( 2016 ) Synthesis and microstructuredependent photoactivated properties of three-dimensional cadmium sulfide crystals . J Alloy Compd 688 : 769 - 775 28. Jana A , Ghosh S , Devi PS , Bandyopadhyay NR , Ray M ( 2014 ) Tunable charge transport through n-ZnO nanorods on Au coated macroporous p-Si . J Mater Chem C 2 : 9613 - 9619 29. Miller DR , Akbar SA , Morris PA ( 2014 ) Nanoscale metal oxide-based heterojunctions for gas sensing: a review . Sens Actuators B 204 : 250 - 272 30. Khanchandani S , Kundu S , Patra A , Ganguli AK ( 2013 ) Band gap tuning of ZnO/In2S3 core/shell nanorod arrays for enhanced visible-light-driven photocatalysis . J Phys Chem C 117 : 5558 - 5567 31. Dai XJ , Luo YS , Zhanga WD , Fu SY ( 2010 ) Facile hydrothermal synthesis and photocatalytic activity of bismuth tungstate hierarchical hollow spheres with an ultrahigh surface area . Dalton Trans 39 : 3426 - 3432 32. Han C , Yang MQ , Weng B , Xu YJ ( 2014 ) Improving the photocatalytic activity and anti-photocorrosion of semiconductor ZnO by coupling with versatile carbon . Phys Chem Chem Phys 16 : 16891 - 16903 33. Jin B , Jiao Z , Bi Y ( 2015 ) Efficient charge separation between Bi2MoO6 nanosheets and ZnO nanowires for enhanced photoelectrochemical properties . J Mater Chem A 3 : 19702 - 19705 34. Liang YC , Chung CC , Lo YJ , Wang CC ( 2016 ) Microstrucrue-dependent visible-light driven photoactivity of sputtering-assisted synthesis of sulfidebased visible-light sensitizer onto ZnO nanorods . Materials 9:1014


This is a preview of a remote PDF: http://link.springer.com/content/pdf/10.1186%2Fs11671-017-2022-z.pdf

Photoexcited Properties of Tin Sulfide Nanosheet-Decorated ZnO Nanorod Heterostructures, Nanoscale Research Letters, 2017, DOI: 10.1186/s11671-017-2022-z