Strong and Ductile Non-equiatomic High-Entropy Alloys: Design, Processing, Microstructure, and Mechanical Properties

JOM, Aug 2017

We present a brief overview on recent developments in the field of strong and ductile non-equiatomic high-entropy alloys (HEAs). The materials reviewed are mainly based on massive transition-metal solute solutions and exhibit a broad spectrum of microstructures and mechanical properties. Three relevant aspects of such non-equiatomic HEAs with excellent strength–ductility combination are addressed in detail, namely phase stability-guided design, controlled and inexpensive bulk metallurgical processing routes for appropriate microstructure and compositional homogeneity, and the resultant microstructure–property relations. In addition to the multiple principal substitutional elements used in these alloys, minor interstitial alloying elements are also considered. We show that various groups of strong and ductile HEAs can be obtained by shifting the alloy design strategy from single-phase equiatomic to dual- or multiphase non-equiatomic compositional configurations with carefully designed phase instability. This design direction provides ample possibilities for joint activation of a number of strengthening and toughening mechanisms. Some potential research efforts which can be conducted in the future are also proposed.

A PDF file should load here. If you do not see its contents the file may be temporarily unavailable at the journal website or you do not have a PDF plug-in installed and enabled in your browser.

Alternatively, you can download the file locally and open with any standalone PDF reader:

https://link.springer.com/content/pdf/10.1007%2Fs11837-017-2540-2.pdf

Strong and Ductile Non-equiatomic High-Entropy Alloys: Design, Processing, Microstructure, and Mechanical Properties

Strong and Ductile Non-equiatomic High-Entropy Alloys: Design, Processing, Microstructure, and Mechanical Properties ZHIMING LI DIERK RAABE We present a brief overview on recent developments in the field of strong and ductile non-equiatomic high-entropy alloys (HEAs). The materials reviewed are mainly based on massive transition-metal solute solutions and exhibit a broad spectrum of microstructures and mechanical properties. Three relevant aspects of such non-equiatomic HEAs with excellent strength-ductility combination are addressed in detail, namely phase stability-guided design, controlled and inexpensive bulk metallurgical processing routes for appropriate microstructure and compositional homogeneity, and the resultant microstructure-property relations. In addition to the multiple principal substitutional elements used in these alloys, minor interstitial alloying elements are also considered. We show that various groups of strong and ductile HEAs can be obtained by shifting the alloy design strategy from single-phase equiatomic to dual- or multiphase non-equiatomic compositional configurations with carefully designed phase instability. This design direction provides ample possibilities for joint activation of a number of strengthening and toughening mechanisms. Some potential research efforts which can be conducted in the future are also proposed. INTRODUCTION Conventional alloy design over the past centuries has been constrained by the concept of one or two prevalent base elements. As a breakthrough of this restriction, the concept of high-entropy alloys (HEAs) containing multiple principal elements has drawn great attention over the last 13 years due to the numerous opportunities for investigations in the huge unexplored compositional space of multicomponent alloys.1–6 A large number of studies in this field have been motivated by the original HEA concept, which suggested that achieving maximized configurational entropy using equiatomic ratios of multiple principal elements could stabilize singlephase massive solid-solution phases.1 However, an increasing number of studies have revealed that formation of single-phase solid solutions in HEAs shows weak dependence on maximization of the configurational entropy through equiatomic ratios of elements,7–10 and it was even found that maximum entropy is not the most essential parameter when designing multicomponent alloys with superior properties.11,12 These findings encouraged efforts to relax the unnecessary restrictions on both the equiatomic ratio of multiple principal elements as well as the formation of single-phase solid solutions. In this context, nonequiatomic HEAs with single-, dual-, or multiphase structure have recently been proposed to explore the flexibility of HEA design and overcome the limitations of the original HEA design concept.4,13,14 Also, deviation from the equimolar composition rule facilitates identification of compositions which allow the often-brittle intermetallic phases to be avoided. Thermodynamic investigations of non-equiatomic HEAs showed that the configurational entropy curve of these alloys is rather flat, indicating that a wide range of compositions alongside the equiatomic configuration assume similar entropy values.15 As illustrated schematically in Fig. 1, compared with conventional alloys with one or two principal elements plus minor alloying components, as well as equiatomic HEAs with equimolar ratios of all alloy elements, non-equiatomic HEAs greatly expand the compositional space that can be probed. Indeed, recent studies have revealed that outstanding mechanical properties exceeding those of equiatomic HEAs can be achieved by non-equiatomic alloys.4,13 As one of the possible pathways, a novel type of transformation-induced plasticity-assisted dualphase (TRIP-DP) HEA was developed.4 The two constituent phases in the alloy, i.e., the face-centered cubic (FCC) matrix and the hexagonal close-packed (HCP) phase, are compositionally equivalent and thus can both be referred to as high-entropy phases.4 This leads to a significantly improved strength– ductility combination compared with corresponding equiatomic HEAs, mainly due to the combination of massive solid-solution strengthening and the TRIP effect.4,13 The above-mentioned findings clearly indicate that expanding the HEA design concept to nonequiatomic compositions has great potential for pursuing more compositional opportunities for design of novel materials with exceptional properties. We aim herein to provide a brief overview on some recent developments of various strong and ductile nonequiatomic HEAs, placing specific attention on their compositional design, metallurgical processing routes, and microstructure–property relations. Some pending directions in this field, e.g., multifunctionalities of various non-equiatomic HEAs, are also pointed out. COMPOSITIONAL DESIGN OF STRONG AND DUCTILE NON-EQUIATOMIC HIGH-ENTROPY ALLOYS Since the majority of the research effort in the field of HEAs during the last decade has focused on single-phase solid solutions, compositional design criteria for achieving single-phase solid solutions have been well explored; For instance, it was proposed that valence electron concentration (VEC) is a critical parameter determining the stability of single-phase FCC (VEC ‡ 8) and bodycentered cubic (BCC) (VEC < 6.87) solid solutions.16 However, the limited hardening mechanisms available in single-phase HEAs, i.e., primarily dislocation interaction and solid-solution strengthening, restrict their strain-hardening capacity as well as the attainable strength–ductility combination. Using the concept of non-equiatomic HEAs, one can tune the compositions of certain HEA systems to introduce multiple deformation mechanisms, thereby improving the range of strength–ductility combinations accessible. This is attributed to the fact that high ductility of strong metallic alloys can be obtained when different deformation mechanisms are activated sequentially during ongoing loading, such as the additional activation of twinning and phase transformation at higher deformations known from twinning-induced plasticity (TWIP) and TRIP steels.17,18 The TWIP and TRIP phenomena are mainly determined by the value of the stacking fault energy, i.e., the energy carried by the interruption of the normal stacking sequence.19–21 The intrinsic stacking fault energy cI of FCC-structured alloys can be expressed as22 cI ¼ 2qADGFCC!HCP þ 2rFCC!HCP; ð1Þ where DGFCC!HCP is the molar free energy difference between the FCC and HCP phase, qA is the planar packing density (moles/area) of a closepacked plane, and rFCC!HCP is the coherent FCCHCP interfacial energy. For transition metals, the interfacial energy has been assumed to be 10 ± 5 mJ/m2.20,22 The intrinsic stacking fault energy is then mainly determined by the free energy difference between the FCC and HCP phases for compositions of a certain alloy system with similar planar packing density of the close-packed planes. Therefore, both phenomena, i.e., TWIP and TRIP, can be best tuned not by achieving the highest possible entropy-driven thermodynamic stability of the host FCC-structured solid solution but instead by its phase instability related to the free energy difference between the phases, rendering it amenable to athermal transformation mechanisms. Figure 2 shows the free energy differences between the FCC and HCP structures of two typical alloy systems, i.e., quaternary Fe80 xMnxCo10Cr10 (x = 45 at.%, 40 at.%, 35 at.%, and 30 at.%) and quinary Co20Cr20Fe40 yMn20Niy (y = 20 at.%, 15 at.%, 10 at.%, 5 at.%, and 0 at.%), at 300 K derived by thermodynamic calculations using the Calphad approach. Note that parameter-free ab initio simulations, in particular density functional theory calculations, are also powerful to obtain stacking fault energies and/or free energy differences between phases.23 In the quaternary Fe80 xMnxCo10Cr10 system, DGFCC!HCP decreases with reduction of the Mn content (x value) from 45 at.% to 30 at.% (Fig. 2a). Indeed, according to our experimental results,4 the Mn content plays an important role in the phase constitution and phase stability of this alloy system, enabling tuning of displacing transformation mechanisms, i.e., TWIP and TRIP. Specifically, the Fe35Mn45Co10Cr10 alloy has a single FCC structure with dislocation slip as the main deformation mechanism, while Fe40Mn40Co10Cr10 additionally exhibits a TWIP effect of the single FCC structure.9,12 With further decrease of the Mn content, which results in a Fe80-xMnxCo10Cr10 (a) decrease of DGFCC!HCP and hence of the FCC phase stability, the Fe50Mn30Co10Cr10 alloy exhibits partial martensitic transformation of the FCC to the HCP phase upon cooling from the high-temperature single-phase region,4,13 with the formation of a dualphase HEA composed of two phases of identical chemical composition, i.e., high-entropy phases. This enables significant enhancement of both the strength and ductility of the quaternary Fe80 xMnxCo10Cr10 system.4 Analogously, DGFCC!HCP decreases significantly with reduction of the Ni content (y value) from 20 at.% to 0 at.% in the quinary Co20Cr20Fe40 yMn20Niy system (Fig. 2b). According to recent experimental results,23 the structure of the alloy accordingly shifts from single FCC phase to dual phase (FCC and HCP) at the homogenized state without strain loading when decreasing the Ni content in the Co20Cr20Fe40 yMn20Niy system from 20 at.% to 6 at.%. Except for the dual-phase structure, the resultant non-equiatomic Co20Cr20Fe34Mn20Ni6 alloy also exhibits the TRIP effect and hence higher tensile strength and strain-hardening ability compared with the corresponding equiatomic reference Co20Cr20Fe20Mn20Ni20 alloy.23 This indicates that the TRIP-DP effect introduced into the former quaternary alloy can also be realized in quinary alloys with higher mixing entropy value. When designing the composition of strong and ductile non-equiatomic dual- or multiphase HEAs, it is also essential to note that the multiple principal elements selected should be distributed uniformly in the microstructure, or at least partition in such a way that all of the coexisting phases have a high solid-solution effect and high mixing entropy. This was not achieved in previous studies, where dual- or multiphase structures were rather formed by elemental segregation, generally leading to undesired brittle intermetallic compounds.3 From this point of view, deformation-driven partial athermal martensitic transformation without associated chemical gradients across phase boundaries is likely to be a well-suited approach for producing dual- or multiphase HEAs with uniformly distributed multiple principal elements. The TRIP-DP effect explained above for addressing the strength–ductility tradeoff can also be introduced into other types of HEAs such as the refractory metal TiNbTaZrHf system via a ‘‘d-electron alloy design’’ approach where athermal transitions between the BCC and the HCP phases are conceivable.24 Furthermore, minor interstitial element fractions can also be introduced into strong and ductile nonequiatomic dual- or multiphase HEAs to further improve their mechanical properties. We added carbon as interstitial element into a TRIP-DP-HEA in the pursuit of two main trends25: (i) that addition of interstitial carbon leads to a slight increase in stacking fault energy and hence phase stability, enabling tuning of the FCC matrix phase stability to a critical point so as to trigger the TWIP effect while maintaining the TRIP effect, thereby further improving the alloy’s strain-hardening ability; (ii) that HEAs can benefit profoundly from interstitial solid-solution strengthening with its huge local distortions instead of only the established massive substitutional solidsolution strengthening provided by its multiple principal elements. Thus-prepared interstitial HEA (referred to as iHEA) was indeed characterized by a combination of various strengthening mechanisms including interstitial and substitutional solid solution, TWIP, TRIP, nanoprecipitates, dislocation interactions, stacking faults, and grain boundaries, leading to twice the tensile strength compared with the equiatomic Co20Cr20Fe20Mn20Ni20 reference HEA while maintaining identical ductility.25 PROCESSING OF STRONG AND DUCTILE BULK NON-EQUIATOMIC HIGH-ENTROPY ALLOYS For 3d transition-metal HEAs, well-established bulk metallurgical processes are available to synthesize high-quality alloy sheets when the Fig. 3. Processing routes and related parameters as well as resultant compositional homogeneity states for 3d transition-metal highentropy alloys. thermomechanical processing parameters are controlled in a proper way. As shown in Fig. 3, we used a vacuum induction furnace to melt and cast various transition-metal HEAs. Except for traditional casting setups, the recently developed combinatorial approach, referred to as rapid alloy prototyping (RAP),26 can also be employed for rapid trend screening of suitable alloy compositions. The RAP technique enables synthesis of five different alloys with tuned compositions of the alloy system in one operation by using a set of five copper molds which can be moved stepwise inside the furnace.26 In as-cast condition, the multiple principal elements are typically not homogeneously distributed in the bulk HEAs with their coarse dendritic microstructure owing to classical Scheil segregation, although x-ray diffraction (XRD) analysis may suggest single- or dual-phase structures.27 Following casting, alloy plates are cut from the cast blocks and hot-rolled at 900 C with total thickness reduction of 50% to remove the dendritic microstructure and possible inherited casting defects. The hotrolling temperature can be adjusted to higher values depending on the specific alloy compositions. Often, even such hot-rolled HEAs still show some retained compositional inhomogeneity. The hotrolled alloy sheets are thus homogenized at 1200 C for more than 2 h followed by water quenching. The homogenization time should be extended according to the dimensions of the alloy sheets; i.e., the larger the alloy sheet, the longer the homogenization time. Such homogenized HEA sheets generally show homogeneous distribution of the multiple principal elements and no cracks or pores. However, for HEAs containing high amount of Mn (e.g., >10 at.%), there would be a few inclusions enriched in Mn, which are very hard to remove even by long-term homogenization. Since homogenized HEA sheets exhibit huge grain size (>30 lm), cold-rolling and annealing processes are generally required to refine the grains to achieve better mechanical properties. We coldrolled homogenized alloy sheets to total thickness reduction of 60% and annealed them at 900 C for different time periods. Annealing was conducted to obtain full recrystallization of the microstructure and to control the grain sizes, hence times and temperatures were adjusted in each case according to the targeted grain sizes and textures. Long-term annealing treatments (e.g., 500 days) at intermediate temperatures (e.g., 700 C and 500 C) can lead to chemical segregations even for the single-phase equiatomic CoCrFeMnNi HEA.8 Interestingly, for the recently designed TRIPassisted dual-phase HEAs,13 annealing treatments can be used not only to control the grain size, but also to modify the phase fractions in the microstructure. Figure 4 shows the variations in the FCC grain size and HCP phase fraction of the quaternary adnunale-aplhinagsetiFmee50aMtn93000CoC10.1C3rI1n0 HcoEldA-rwoliltehdicnocnrdeaitsiionng, the alloy shows average grain size of 250 nm and HCP phase fraction of 91%. After extending the annealing time from 3 min to 60 min, the average FCC grain size increased gradually from 4.5 lm to 17.5 lm. The average HCP phase fraction first drops to 14% from 32% when increasing the annealing time from 3 min to 5 min, then gradually increases to 36% when further increasing the annealing time to 60 min. The underlying mechanisms responsible for this nonmonotonic variation of the HCP phase fraction with increasing annealing time and grain size are discussed in Ref. 13 by considering kinetic factors such as nucleation of the HCP phase and blocking effects of grain boundaries. Grain size and phase fractions significantly influence the deformation behavior of dual-phase HEAs, suggesting that a well-tuned annealing process is pivotal for achieving desired excellent strength– ductility combinations in these alloys. Processing routes are not only decisive for the grain size and phase fraction corresponding to a targeted specific composition, but are also critical with respect to the compositional homogeneity state, which also has significant effects on the mechanical behavior. We applied various processing routes including hot-rolling, homogenization, coldrolling, and recrystallization annealing on cast alloys to obtain samples in different compositional homogeneity states.27 In the case of coarse grains ( 300 lm) obtained for as-cast alloys without homogenization treatment, the ductility and strain hardening of the material were significantly reduced due to the compositional inhomogeneity. This detrimental effect was attributed to preferred deformation-driven phase transformation occurring in the Fe-enriched regions with lower stacking fault energy, promoting early stress–strain localization.27 The grain-refined structure ( 4 lm) with compositional heterogeneity obtained for annealed alloys without any preceding homogenization treatment was characterized by almost total loss of work %80 , n o itc60 a r f se40 a h p P20 C H hardening. This effect was attributed to large local shear strains due to inhomogeneous planar slip.27 These findings demonstrate the importance of processing routes for the development of strong and ductile HEAs. MICROSTRUCTURE AND MECHANICAL PROPERTIES OF NON-EQUIATOMIC HIGH-ENTROPY ALLOYS Similar to the single-phase equiatomic Co20Cr20Fe20Mn20Ni20 alloy, the single-phase non-equiatomic Fe40Mn27Ni26Co5Cr2,11 Fe35Mn45Co10Cr10,9 and Fe40Mn40Co10Cr1012 alloys can also form a fully recrystallized microstructure containing a large amount of annealing twins in equiaxed matrix grains with uniformly distributed elements when using appropriate processing routes as explained above. When shifting the single-phase non-equiatomic HEAs to dual-phase non-equiatomic HEAs and further to interstitially alloyed HEAs (iHEAs), the complexity of the microstructure gradually increases. Figure 5 shows the typical microstructures of the non-equiatomic Fe50Mn30Co10Cr10 TRIP-DP-HEA4,13 and Fe49.5Mn30Co10Cr10C0.5 TRIP-TWIP-iHEA25 as revealed by electron backscatter diffraction (EBSD), electron channeling contrast imaging (ECCI), atom probe tomography (APT), and transmission electron microscopy (TEM) techniques. The TRIP-DP-HEA consists of two phases, namely FCC c matrix and HCP e phase (Fig. 5a1). The HCP e phase is formed within the FCC c matrix and mainly exhibits laminate morphology (Fig. 5a1–2). Annealing twins, stacking faults, and dislocations are also present in the FCC c matrix in recrystallized state.4,13 With addition of C, the fraction of HCP e phase in the iHEA is significantly reduced after annealing (Fig. 5b1) compared with the reference alloy without C (Fig. 5a1). This is due to the slight increase of stacking fault energy and correspondingly higher FCC phase 24 21 18 15 12 9 6 3 0 m μ , e z i s n i a r g C C F stability with addition of C. A large amount of annealing twins can also be observed in the iHEA in annealed state (Fig. 5b1). Also, particles with average size of 50–100 nm and volume fraction of 1.5 vol.% are observed (Fig. 5b2–6). These particles were determined to be M23C6 carbides (M: Cr, Mn, Fe, and Co) with FCC structure according to APT (Fig. 5b3–4) and TEM (Fig. 5b5–6) probing. Figure 6 summarizes the ultimate tensile strength and total elongation data obtained from various transition-metal HEAs. The homogenized singlephase non-equiatomic Fe40Mn27Ni26Co5Cr2 (#1)11 alloy shows ultimate strength and total elongation values similar to the homogenized single-phase equiatomic Co20Cr20Fe20Mn20Ni20 alloy (#2),23 even though the former has finer grain size (35 versus 140 lm; Fig. 7). The trend is similar for the homogenized non-equiatomic Fe35Mn45Co10Cr10 alloy (#3). One of the key mechanisms behind this trend is that twinning can occur in the single-phase equiatomic Co20Cr20Fe20Mn20Ni20 alloy to a certain extent, while mere dislocation hardening prevails in the nonequiatomic Fe40Mn27Ni26Co5Cr2 (#1)11 and Fe35Mn45Co10Cr10 (#3) alloys upon tensile deformation at room temperature. Interestingly, the homogenized singlephase non-equiatomic Fe40Mn40Co10Cr10 alloy (#4) shows significantly higher ultimate strength ( 95 MPa) compared with the equiatomic alloy (#2) due to the introduction of a higher extent of twinning behavior.12 Along with the alloy design strategies explained above, the newly designed quinary TRIPassisted dual-phase Co20Cr20Fe34Mn20Ni6 alloy (#5)23 has further enhanced ultimate strength compared with the TWIP-assisted Fe40Mn40Co10Cr10 alloy (#4). Furthermore, the homogenized dual-phase nonequiatomic Fe50Mn30Co10Cr10 alloy (Fig. 6; #6) shows much higher ultimate strength compared with the various single-phase alloys (#1–4) and the dualphase Co20Cr20Fe34Mn20Ni6 alloy (#5), while maintaining total elongation above 50%. Interestingly, the alloy with the same composition but refined FCC matrix grains (#7) exhibits further significant joint increase of strength and ductility. This is ascribed to the substantially improved work-hardening ability of the alloy due to the well-tuned phase stability via adjustment of grain size and phase fractions.4,13 With addition of interstitial element carbon into the dualphase microstructure, the grain-refined Fe49.5Mn30Co10Cr10C0.5 alloy (#8) shows further increased ultimate strength up to nearly 1 GPa with total elongation of 60%. These superior mechanical properties are attributed to the joint activity of various strengthening mechanisms including interstitial and substitutional solid solution, TWIP, TRIP, nanoprecipitates, dislocation interactions, stacking faults, and grain boundaries.25 To further clarify the mechanisms responsible for the above microstructure–property relations, Fig. 7 provides an overview of the various deformation mechanisms in different multicomponent HEAs presented in Fig. 6. From the single-phase Fe40Mn27Ni26Co5Cr2 and Fe35Mn45Co10Cr10 alloys towards the single-phase Co20Cr20Fe20Mn20Ni20 and Fe40Mn40Co10Cr10 alloys, a TWIP effect has been introduced. Then, the presence of phase boundaries (dual-phase structure) and the TRIP effect are included in the dual-phase Co20Cr20Fe34Mn20Ni6 and Fe50Mn30Co10Cr10 alloys. Proceeding further to the carbon-containing Fe49.5Mn30Co10Cr10C0.5 alloy, interstitial solid solution and nanoprecipitate strengthening effects are additionally utilized, thereby unifying all known strengthening mechanisms in one material. Indeed, these multiple deformation mechanisms enable significant improvement of the strain-hardening capacity and strength–ductility combination. This clearly shows that tuning deformation mechanisms via composition adjustment is key to the design of strong and ductile non-equiatomic HEAs. Therefore, we suggest that introduction of multiple deformation mechanisms which are activated gradually or, respectively, sequentially during mechanical and/or thermal loading is a key route for future development of new HEAs with advanced mechanical properties. Such a concept can be realized by shifting from single-phase equiatomic to dualor multiphase non-equiatomic compositional configurations. SUMMARY AND OUTLOOK We have presented a brief overview on the design, processing, microstructure, and mechanical properties of non-equiatomic HEAs. As the most widely studied HEA family, we mainly focused on 3d transition-metal HEAs, which exhibit a broad spectrum of microstructures and mechanical behavior. We showed that various strong and ductile HEAs can be obtained by shifting the alloy design strategy from single-phase equiatomic to dual- or multiphase nonequiatomic compositions. The non-equiatomic HEA concept provides possibilities for the unification of various strengthening and toughening mechanisms, enabling significant improvement of strain-hardening capacity and strength–ductility combinations. To design strong and ductile non-equiatomic transitionmetal HEAs, the intrinsic stacking fault energies and/or the free energy differences between the FCC and HCP phases for various compositions can be probed in an effort to tune the phase stabilities by adjusting the compositions. Proper processing routes toward homogeneously distributed multiple principal elements and appropriate grain sizes are also important for achieving targeted strength–ductility combinations, especially for dual-phase non-equiatomic HEAs with TRIP effect. Although outstanding strength and ductility have been achieved in several non-equiatomic transitionmetal HEAs, e.g., ultimate tensile strength of 1 GPa and total elongation of 60% in the abovementioned TWIP-TRIP-iHEA at room temperature, further research into strong and ductile nonequiatomic HEAs is still required; possible future trends include: 1. The strength and ductility of the various nonequiatomic HEAs at low and elevated temperatures are still unknown, and new (non-equiatomic) HEAs with excellent strength–ductility combinations at low and elevated temperatures can be designed and studied. 2. For the widely studied transition-metal HEAs with their good strength–ductility combinations, other properties such as the resistance to hydrogen-induced degradation,28,29 corrosion resistance, fatigue behavior, and magnetic performance can also be explored in an effort to find superior combinations of properties, i.e., multifunctionalities, to justify their relatively high cost compared with established high-strength and austenitic stainless steels. Also, following the design approach associated with the stacking fault energies and/or the free energies, a shape-memory effect could be introduced into non-equiatomic HEAs. ACKNOWLEDGEMENTS Open access funding provided by Max Planck Society. The authors would like to acknowledge the financial support by the European Research Council under the EU’s 7th Framework Programme (FP7/ 2007–2013) and the contributions of Konda Gokuldoss Pradeep, Cemal Cem Tasan, Yun Deng, Mengji Yao, Hauke Springer, Fritz Ko¨rmann, Blazej Grabowski, and Jo¨rg Neugebauer. OPEN ACCESS This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/ ), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. 1. J.W. Yeh , S.K. Chen , S.J. Lin , J.Y. Gan , T.S. Chin , T.T. Shun, C.H. Tsau , and S.Y. Chang , Adv. Eng. Mater. 6 , 299 ( 2004 ). 2. B. Cantor , I.T.H. Chang , P. Knight , and A.J.B. Vincent , Mater. Sci. Eng. A 375-377 , 213 ( 2004 ). 3. Y. Zhang , T.T. Zuo , Z. Tang , M.C. Gao , K.A. Dahmen , P.K. Liaw , and Z.P. Lu , Prog. Mater. Sci. 61 , 1 ( 2014 ). 4. Z. Li , K.G. Pradeep , Y. Deng , D. Raabe , and C.C. Tasan , Nature 534 , 227 ( 2016 ). 5. F. Otto , A . Dlouhy´, C. Somsen , H. Bei , G. Eggeler, and E.P. George , Acta Mater. 61 , 5743 ( 2013 ). 6. D.B. Miracle and O.N. Senkov , Acta Mater. 122 , 448 ( 2017 ). 7. Y.P. Wang , B.S. Li , and H.Z. Fu , Adv. Eng. Mater. 11 , 641 ( 2009 ). 8. F. Otto , A . Dlouhy´, K.G. Pradeep , M. Kubeˇnov a´, D. Raabe , G. Eggeler, and E.P. George , Acta Mater. 112 , 40 ( 2016 ). 9. C.C. Tasan , Y. Deng , K.G. Pradeep , M.J. Yao , H. Springer, and D. Raabe , JOM 66 , 1993 ( 2014 ). 10. F. Otto , Y. Yang , H. Bei , and E.P. George , Acta Mater. 61 , 2628 ( 2013 ). 11. M.J. Yao , K.G. Pradeep , C.C. Tasan , and D. Raabe , Scr. Mater. 72 - 73 , 5 ( 2014 ). 12. Y. Deng , C.C. Tasan , K.G. Pradeep , H. Springer, A. Kostka, and D. Raabe , Acta Mater. 94 , 124 ( 2015 ). 13. Z. Li , C.C. Tasan , K.G. Pradeep , and D. Raabe , Acta Mater. 131 , 323 ( 2017 ). 14. K.G. Pradeep , C.C. Tasan , M.J. Yao , Y. Deng , H. Springer, and D. Raabe , Mater. Sci. Eng., A 648 , 183 ( 2015 ). 15. D. Ma, M. Yao , K.G. Pradeep , C.C. Tasan , H. Springer, and D. Raabe , Acta Mater. 98 , 288 ( 2015 ). 16. S. Guo , C. Ng , J. Lu , and C.T. Liu, J. Appl. Phys . 109 , 103505 ( 2011 ). 17. I. Gutierrez-Urrutia and D. Raabe , Acta Mater. 59 , 6449 ( 2011 ). 18. C. Herrera , D. Ponge , and D. Raabe , Acta Mater. 59 , 4653 ( 2011 ). 19. D. Raabe , F. Roters , J. Neugebauer , I. Gutierrez-Urrutia , T. Hickel , W. Bleck , J.M. Schneider , J.E. Wittig , and J. Mayer , MRS Bull . 41 , 320 ( 2016 ). 20. A. Saeed-Akbari , J. Imlau , U. Prahl , and W. Bleck , Metall. Mater. Trans. A 40 , 3076 ( 2009 ). 21. T. Hickel , S. Sandlo¨bes, R.K.W. Marceau , A. Dick , I. Bleskov , J. Neugebauer , and D. Raabe , Acta Mater. 75 , 147 ( 2014 ). 22. P.H. Adler , G.B. Olson , and W.S. Owen , Metall. Mater. Trans. A 17 , 1725 ( 1986 ). 23. Z. Li , F. Ko ¨rmann, B. Grabowski , J. Neugebauer , and D. Raabe , Acta Mater. 136 , 262 ( 2017 ). 24. L. Lilensten , J.-P. Couzinie´ , J. Bourgon , L. Perrie`re, G. Dirras, F. Prima , and I. Guillot , Mater. Res. Lett. 5 , 110 ( 2017 ). 25. Z. Li , C.C. Tasan , H. Springer, B. Gault , and D. Raabe , Sci. Rep . 7 , 40704 ( 2017 ). 26. H. Springer and D. Raabe , Acta Mater. 60 , 4950 ( 2012 ). 27. Z. Li and D. Raabe , Mater. Chem. Phys. ( 2017 ). doi: 10 .1016/ j.matchemphys. 2017 . 04 .050. 28. H. Luo , Z. Li , Y.-H. Chen , D. Ponge , M. Rohwerder , and D. Raabe , Electrochem. Commun. 79 , 28 ( 2017 ). 29. H. Luo , Z. Li , and D. Raabe , Sci. Rep . ( 2017 ). doi:10.1038/ s41598-017-10774-4. 30. M.C. Gao , C.S. Carney , O¨ .N. Dog ˘an, P.D. Jablonksi , J.A. Hawk , and D.E. Alman , JOM 67 , 2653 ( 2015 ).


This is a preview of a remote PDF: https://link.springer.com/content/pdf/10.1007%2Fs11837-017-2540-2.pdf

Zhiming Li, Dierk Raabe. Strong and Ductile Non-equiatomic High-Entropy Alloys: Design, Processing, Microstructure, and Mechanical Properties, JOM, 2017, 1-8, DOI: 10.1007/s11837-017-2540-2