Use of Oxalic-Acid-Modified Stellerite for Improving the Filter Capability of PM2.5 of Paper Composed of Bamboo Residues

International Journal of Polymer Science, Dec 2016

In this study, pulping conditions for kraft pulping of bamboo residues were investigated, predominantly focusing on cooking temperature and time during pulping. Oxalic acid and cationic starch were used for the modification of natural stellerite, and the use of modified stellerite for preparing filter paper for PM2.5 filtration was investigated. The optimal pulping technology of bamboo residues was established based on the following experimental parameters: liquor ratio of 1 : 5.5, cooking temperature of 160°C, and a holding time of 2 h. Modification by oxalic acid resulted in the promotion of pore formation at the stellerite surfaces and induced the microscopic changes. Nevertheless, paper strength remained practically unchanged after the addition of fillers, indicating that the cationic starch preblend method is a promising technique for papermaking because it enhances the strength properties of paper. With the variation in the addition of modified stellerite from 3 to 15%, while simultaneously maintaining the basis weight constant at 60 gm−2, the filtration efficiency of paper sheets first increased and then decreased later; thus the optimum stellerite content was found to be 9%. Filtration efficiency was suggested to be affected by gas flowing velocity.

A PDF file should load here. If you do not see its contents the file may be temporarily unavailable at the journal website or you do not have a PDF plug-in installed and enabled in your browser.

Alternatively, you can download the file locally and open with any standalone PDF reader:

http://downloads.hindawi.com/journals/ijps/2016/2198506.pdf

Use of Oxalic-Acid-Modified Stellerite for Improving the Filter Capability of PM2.5 of Paper Composed of Bamboo Residues

Use of Oxalic-Acid-Modified Stellerite for Improving the Filter Capability of PM2.5 of Paper Composed of Bamboo Residues Hua Chen,1,2,3 Jian Lou,1 Fei Yang,4 Jia-nan Zhou,1 Yan Zhang,1 and Huabo Yao1 1Zhejiang Provincial Key Lab for Chem & Bio Processing Technology of Farm Product, Key Laboratory of Recycling and Eco-Treatment of Waste Biomass of Zhejiang Province, Zhejiang University of Science and Technology, Hangzhou 310023, China 2Key Laboratory of Pulp and Paper Science & Technology of Ministry of Education of China, Qilu University of Technology, Jinan 250353, China 3Zhejiang Yongtai Paper Co. Ltd, Hangzhou 311421, China 4State Key Lab of Pulp and Paper Engineering, South China University of Technology, Guangzhou 510640, China Received 5 October 2016; Accepted 21 November 2016 Academic Editor: Weifeng Zhao Copyright © 2016 Hua Chen et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. Abstract In this study, pulping conditions for kraft pulping of bamboo residues were investigated, predominantly focusing on cooking temperature and time during pulping. Oxalic acid and cationic starch were used for the modification of natural stellerite, and the use of modified stellerite for preparing filter paper for PM2.5 filtration was investigated. The optimal pulping technology of bamboo residues was established based on the following experimental parameters: liquor ratio of 1 : 5.5, cooking temperature of 160°C, and a holding time of 2 h. Modification by oxalic acid resulted in the promotion of pore formation at the stellerite surfaces and induced the microscopic changes. Nevertheless, paper strength remained practically unchanged after the addition of fillers, indicating that the cationic starch preblend method is a promising technique for papermaking because it enhances the strength properties of paper. With the variation in the addition of modified stellerite from 3 to 15%, while simultaneously maintaining the basis weight constant at 60 gm−2, the filtration efficiency of paper sheets first increased and then decreased later; thus the optimum stellerite content was found to be 9%. Filtration efficiency was suggested to be affected by gas flowing velocity. 1. Introduction With the economic development of China as well as the growth of its transportation industry, air pollution is becoming more serious in recent years. Several contaminants and pollutants can be adsorbed on the particles suspended in the atmosphere and enter the body via respiration. Most studies have reported that PM2.5 (particles with an aerodynamic diameter of 2.5 μm or less) [1] with small average particles size, large-scale impact, and high specific surface area can enter the human respiratory system and even penetrate through the lung cells into blood circulation, posing serious hazards to human health [2], including asthma [3] and bronchitis [4]. More importantly studies have increasingly reported that PM2.5 possibly stimulates the mutation of the p53 gene in nasopharyngeal epithelial cells and plays an important role in the carcinogenesis of oral tissues [5]. According to the American Cancer Society, an 8% increase in cancer mortality for every 10 μgm−3 increase in PM2.5 consistency for city population has been observed. On the other hand, China has the richest resources of bamboo in the world, where 33,000 km2 or 3% of the country’s total forest area is occupied by bamboo [6]. With the development of the bamboo industry, a large number of residues are produced, and the utilization of these bamboo residues is not greater than 10%, where its collecting and treatment has noticed by people [7]. Both domestic and international studies have indicated that fiber filter material exhibits several advantages, such as mass production, low cost, high surface area, porous nature, and good flexibility [8–12]. The main raw materials used for filter material for high-efficiency PM2.5 capture include natural plant, synthetic fiber, glass, ceramic, and metal fibers. Natural plant fiber, such as bamboo residues, is probably the most promising one among various PM2.5 filter materials, attributed to its wide spread sources, low cost, and excellent reprocessing performance. Zeolite is a type of aqueous silicoaluminate mineral with excellent adsorption characteristics. Porous zeolites have been widely used in catalysis, adsorption, and separation attributed to their open frameworks, high surface areas, and ordered pore structures [13–15]. Nevertheless, few studies have been reported on natural zeolite, despite its low cost and abundant storage [16]. In this study, the effect of filter paper made from bamboo residue and oxalic-acid-modified stellerite on PM2.5 filtration was comprehensively investigated. Factors affecting pulping and the use of stellerite were also investigated. 2. Experimental2.1. Materials2.1.1. Raw Materials Stellerite was purchased from Jinshansida Co., Ltd. (Guilin, China). Oxalic acid, sodium hydroxide (NaOH), and sodium sulfide nonahydrate (Na2S·9H2O) with purities of 96% were supplied by Linfeng Chemical Co., Ltd. (Shanghai, China). Cationic starch with a substitution degree of 0.028 was purchased from Hengfeng Chemical Co., Ltd. (Zhejiang, China). Bamboo (Bambusa rigida species) residue was provided by a bamboo products company (Anji, China). The residue exhibited the following average characteristics: 49.96% cellulose, 22.88% total lignin, and 17.97% hemicelluloses. 2.1.2. Pulping and Beating First, bamboo residue (abbreviated as BR) was crushed and screened through a mesh with a size of 160. According to ISO 287-1985 standard, its moisture content was determined to be 12.27%. Pulping was conducted by the kraft pulping method with a liquor ratio of 1 : 5.5, active alkali of 30%, and a sulfureted degree of 30%. Samples were referred to as P1, P2, P3, P4, P5, and P6 according to the cooking process as shown in Table 1. Table 1: Cooking process. Filtration and washing were conducted after pulping. Finally, the pulp was refined to 30°SR using a TD7 Refiner (TD7-PFI, SUST, Shanxi, China). 2.1.3. Modification of Stellerite Stellerite was obtained from Jinshansida Co., Ltd. (Guangxi, China). First, stellerite was repeatedly washed using distilled water for removing some impurity ions, and this was followed by dehydration in an oven box at 100°C for 12 h. Second, stellerite (7.5 g) was added into a round flask containing aqueous solution of oxalic acid (150 mL, 1.0 molL−1). Third, the reaction temperature was maintained constant at 85°C for 5 h under stirring. Next, the solid liquid mixture was filtered, and stellerite was washed with distilled water. Further, a AgNO3 test was performed to ensure the absence of remaining Cl− ions in stellerite. After grinding, stellerite was calcined at 105°C for 12 h. 2.1.4. Capping of Cationic Starch Preblend First, distilled water (400 mL) and cationic starch (20 g) were added together in a 500-mL four-necked-round-bottom flask; and the resulting slurry was stirred to ensure sufficient mixing. Second, modified stellerite (20 g) was added to the slurry, and after stirring for 25 min at 90°C, it was dried at 95°C for 12 h. Finally, the mixture was ground into a powder, and cationic-starch-capped modified stellerite was prepared by the preblend method, with a mass ratio of 1 : 1 for cationic starch and modified stellerite. 2.1.5. Preparation of Hand Sheets and Testing First, the beaten pulp was diluted to a consistency of 1.2% using distilled water, followed by disintegration using a standard disintegrator at 20,000 revolutions until all fiber bundles were dispersed. Second, cationic-starch-capped modified stellerite was added under stirring at 3000 revolutions for 1 min, where the concentration of the added fillers was maintained constant at 3, 6, 9, 12, and 15% (based on oven-dry pulp mass). Hand sheets with a target basis weight of 60 gm−2 were prepared using the ZBJ1-B Automatic Sheet Former System (SUST, Shanxi, China) according to TAPPI T 205 (TAPPI Test Methods, 2002), with the exception that the pressure utilized for wet sheet pressing was controlled at 200 kPa, followed by drying at 102°C using a Formax 12′′ Drum Dryer (Thwing-Albert Instrument, USA). The hand sheets were conditioned under a controlled environment (temperature of °C and relative humidity of %) before analysis. The tensile index and air permeability of hand sheets were determined according to the relevant TAPPI Standards. The tensile index of the paper sheets was determined using a WZL-300B Tensile Strength Tester (Qitongboke, China), and air permeability was tested using an Air Permeance Tester (Messmer Instruments Ltd., Testing Machines Inc., USA). The ash content of the fibers was measured according to ISO 2144:1997 method, and the ash content of the pulp and paper sheets was determined according to TAPPI T 413 om-85 (1985) standards. The retention efficiency of the fillers was calculated by using Here, , , and represent the ash content of the paper sheets, fiber, and pulp, respectively, and represents the loss on ignition of stellerite. Filtration efficiencies of various hand sheets were investigated using TSI-8130 Automated Filter Tester (TSI Company, USA). The 0.3 μm NaCl particle was used as the filtration simulation model (adjusted flow of 32 Lmin−1). 2.1.6. Determination of Pore Distribution A pore size distribution detector ASAP2010M (Micromeritics, USA) was used for the structural analyses of fiber pores. High-purity N2 was used as the adsorbate, and the adsorption–desorption of high-purity N2 was determined at 77 K in a liquid nitrogen trap by a static volumetric method. 2.1.7. Fourier Transform Infrared Spectroscopy Analysis Fourier transform infrared (FTIR) spectroscopy analysis of the samples was conducted in the transmission mode by macrotechniques (13 mmΦ pellet; ca. 1.5 mg sample with 350 mg KBr). The spectra were recorded using a Nexus Vector spectrometer (Nexus 670, Thermo Nicolet Company, USA) under the following specifications: Apodization: triangular; detector: DTGS/KBr; regulation: 4 cm−1; and number of scans: 32. 2.1.8. X-Ray Diffraction Analysis The X-ray powder diffraction (XRD) patterns of the samples were recorded on a Bruker D8 Advance XRD instrument (step size of 0.02° with 17.7 s per step). A Generator with 40 kV and a current of 40 mA were employed as sources for CuKα radiation. The crystallinity index was calculated from the relative intensities of the diffraction peaks [17] as follows:Here, represents the intensity (°) of the peak belonging to the , which contributes to the strength of the crystalline region, and represents the intensity (°) between the and , which represents the intensity of the amorphous region. 2.1.9. Scanning Electron Microscopy Analysis Morphologies of the hand sheet surfaces were examined by scanning electron microscopy (SEM, JSM-IT300, JEOL, Japan) operating at an accelerating voltage of 15 kV. Before observation, the samples were coated with gold using a vacuum sputter-coater. All experiments were conducted in triplicate with a relative standard deviation (RSD) of approximately 5%. 3. Results and Discussion3.1. Pore Structure Analysis of Fibers and Stellerite Table 2 lists the results obtained from the pore structural analysis of fibers and stellerite. The results indicated that, with increasing cooking degree, surface area and pore volume became greater than the initial volume. Moreover, pore size significantly decreased, indicative of the generation of abundant micropores and mesopores. At this stage, the pulping yield increased because of the reduction in the discharge rate during filtration after cooking. However, cooking for a long time resulted in overcooking, leading to a decrease of surface area and the destruction of the fiber porous structure. Moreover, pulping yield also decreased during overcooking, attributed to the massive reduction of fines in washing process. Thus, the optimal pulping conditions were as follows: cooking temperature of 160°C and a holding time of 2 h (sample P5). Table 2: Pore structure analysis of fibers and stellerite. With respect to the oxalic-acid-modified stellerite, specific surface area () for natural stellerite was 2.2179 m2 g−1; in contrast, for the sample treated with 1.0 mol L−1 oxalic acid, was 108.8327 m2 g−1 (increase by 49 times). In particular, pore size () was also significantly less than that observed for natural stellerite, indicating that a microporous structure was formed. Moreover, the modification yield was 91.41%, attributed to the removal of impurities and loss during washing. 3.2. Functional Group Analysis of Different Samples Figure 1 shows the FTIR spectra of samples BR, P1, P2, P3, P4, P5, and P6. The peak observed at 3447 cm−1 is attributed to the hydroxylgroups (OH) in the fibers; it is a band characteristic of cellulose [18]. The peak observed at 2960 cm−1 is attributed to the C–H absorption. The strong band observed at 1642 cm−1 is attributed to the vibration of absorbed water molecules in the noncrystalline region of cellulose. The band observed at 1511 cm−1 is attributed to the vibration of the aromatic ring of lignin, and the peak observed at 1735 cm−1 is ascribed to the C=O stretching vibration of acetyl and carboxyl of hemicellulose [19]. The comparison of the different spectra indicated that, with increasing cooking degree, the cellulose characteristics of spectra were more apparent, attributed to the fact that, in comparison, cellulose, lignin, and hemicellulose degrade more rapidly in the cooking process. Figure 1: FTIR spectroscopy of different pulp samples: (a) BR, (b) P1, (c) P2, (d) P3, (e) P4, (f) P5, and (g) P6. 3.3. XRD Patterns of Fibers Figure 2(a) shows the XRD patterns of bamboo residues, exhibiting low crystallinity (crystallinity index = 51.8%), as evidenced by their faint pattern. The crystallinity of pulp clearly increased after cooking, with the main peaks observed at 2θ of 22.5° and 18°, attributed to , and the amorphous region of cellulose. Moreover, the crystallinity of P1, P2, P3, P4, P5, and P6 increased to 54.4, 55.6, 56.8, 57.2, 59.9, and 57.8%, respectively. This result is attributed to the following two reasons: the removal of disordered material in the amorphous region and the formation of new crystalline region, ascribed to the realignment of the cellulose chain caused by the penetration of water molecules into the amorphous region [19]. Figure 2: XRD curves of different samples: (a) BR, (b) P1, (c) P2, (d) P3, (e) P4, (f) P5, and (g) P6. 3.4. SEM Images of Different Samples Figure 3 shows the SEM images of different samples, clearly displaying their surface morphology. The bamboo residues consist of piece structure, with several pits randomly distributed on the residue surface (Figure 3(a)). The bamboo fibers with complete shape and clear contours were obtained for the appropriate cooking process (P5, Figure 3(b)). Natural stellerite exhibits a clear layer structure (Figure 3(c)). Treatment with oxalic acid led to the formation of cracks on its surface, resulting in the promotion of pore formation at the stellerite surfaces and induced microscopic changes; this result is consistent with those shown in Table 2 (Figure 3(d)). Figure 3(e) shows the hand sheet without fillers, and Figure 3(f) demonstrates the distribution of granular-modified stellerite between fibers. Figure 3: SEM images of different samples: (a) BR, (b) P5, (c) natural stellerite, (d) modified stellerite, (e) hand sheet composed of P5 without stellerite, and (f) hand sheet composed of P5 with modified stellerite (9%). 3.5. Ash Content and Filler Retention Figure 4 shows the ash content and filler retention of different paper sheets. With increasing stellerite content, ash content increases, and approximately 7.2% of ash was obtained with the addition of 15% stellerite. In contrast, filler retention significantly decreases. Figure 4: Ash content and filler retention of different paper sheets. 3.6. Tensile Indices and Air Permeability of Paper Sheets Figure 5 shows the effects of stellerite content on the tensile indices and air permeability of the paper sheets. Compared to the control (without stellerite), the tensile index of the paper sheet with the addition of 3% stellerite indicated a 3.7% increase; however, the ash content increased from 0.14 to 1.98%. Thus, under experimental conditions employed in this study, appropriate addition of cationic-starch-preblend-modified stellerite exerted a certain positive effect on the tensile index of the paper sheet, possibly attributed to the improvement of evenness. Moreover, with increasing filler content, air permeability also increased. With the addition of 15% stellerite, the air permeability of the paper sheet increased from 3.44 to 6.62 μm Pa−1 s−1, indicating that the porosity of the paper increased because of the addition of filler. Figure 5: Tensile indices and air permeability of paper sheets. 3.7. Filter Performance of Paper Sheets Tables 3 and 4 summarize the filter performance of different paper sheets and the impact of gas flowing velocities. The filter performance was suggested to be affected not only by the dosage of fillers, but also by the gas flowing velocities during testing. The best performance was obtained with the addition of 9% modified stellerite, predominantly attributed to the fact that extremely high air permeability of paper sheets results in the decline of adsorption quantity. This result indicates the existence of an important difference between fibers and fillers in the adsorption of PM2.5. It has been reported that micron wood fibers have low collection efficiency toward particles with the diameter from 0.4 to 0.6 μm, while they have significantly higher collection efficiency for particles with other sizes. Among these particles with the diameter of 0.01 μm, the collection efficiency of micron wood fibers can reach up to 90% [20]. Table 3: Effect of the variation of stellerite content on filter performance. Table 4: Effect of different gas flowing velocities on filter performance. In fact, the filtering process of PM2.5 particles by plant fibers and fillers is very complex and specific to location; therefore, filter performance is affected not only by the -direction position, but also by time. This observation is referred to as layered filtration and nonstationary filtration (see Figure 6), which will be further explored in our future study. Figure 6: Filtration sketch of paper sheets. 4. Conclusions In this study, the following optimum cooking condition of the bamboo residues by kraft pulping was established: a liquor ratio of 1 : 5.5, a cooking temperature of 160°C, and a holding time of 2 h. Modification with oxalic acid resulted in the promotion of pore formation at the stellerite surfaces, which induced microscopic changes while simultaneously maintaining the porous structure of stellerite. The cationic starch preblend method is a promising technique for papermaking as it results in the enhanced strength of paper. The filter performance of paper sheets was significantly increased by the addition of oxalic-acid-modified stellerite. With the addition of 9% oxalic-acid-modified stellerite, the paper sheet exhibited the best filter performance (78.4%) at a gas flowing velocity of 0.2 ms−1. Competing Interests The authors declare that they have no competing interests. Acknowledgments The authors greatly acknowledge the support from the Zhejiang Provincial Natural Science Foundation of China (Grant no. LY15C160002), Zhejiang Provincial Collaborative Innovation Center of Agricultural Biological Resources Biochemical Manufacturing (Grant no. 2016KF0016), and Key Laboratory of Recycling and Eco-Treatment of Waste Biomass of Zhejiang Province (Grant no. 2016REWB12). References W.-B. Xue, F. Fu, J.-N. Wang et al., “Numerical study on the characteristics of regional transport of PM2.5 in China,” China Environmental Science, vol. 34, no. 6, pp. 1361–1368, 2014. View at Google Scholar · View at ScopusB. Luo, H. Shi, L. Wang et al., “Rat lung response to PM2.5 exposure under different cold stresses,” International Journal of Environmental Research and Public Health, vol. 11, no. 12, pp. 12915–12926, 2014. View at Publisher · View at Google Scholar · View at ScopusC. Loftus, M. Yost, P. Sampson et al., “Regional PM2.5 and asthma morbidity in an agricultural community: a panel study,” Environmental Research, vol. 136, pp. 505–512, 2015. View at Publisher · View at Google Scholar · View at ScopusR. Ghosh, P. Rossner, K. Honkova, M. Dostal, R. J. Sram, and I. Hertz-Picciotto, “Air pollution and childhood bronchitis: interaction with xenobiotic, immune regulatory and DNA repair genes,” Environment International, vol. 87, pp. 94–100, 2016. View at Publisher · View at Google Scholar · View at ScopusL. Calderon-Garciduenas, A. Rodriguez-Alcaraz, A. Villarreal-Calderon, O. Lyght, D. Janszen, and K. T. Morgan, “Nasal epithelium as a sentinel for airborne environmental pollution,” Toxicological Sciences, vol. 46, no. 2, pp. 352–364, 1998. View at Publisher · View at Google Scholar · View at ScopusJ. M. O. Scurlock, D. C. Dayton, and B. Hames, “Bamboo: an overlooked biomass resource?” Biomass and Bioenergy, vol. 19, no. 4, pp. 229–244, 2000. View at Publisher · View at Google Scholar · View at ScopusM. He, Y. Zhang, Q. Hu et al., “Comparison of different pretreatment methods for bamboo residues,” Chinese Journal of Appplied Environmental Biology, vol. 17, no. 2, pp. 232–236, 2011. View at Publisher · View at Google ScholarJ. Li, F. Gao, L. Q. Liu, and Z. Zhang, “Needleless electro-spun nanofibers used for filtration of small particles,” Express Polymer Letters, vol. 7, no. 8, pp. 683–689, 2013. View at Publisher · View at Google Scholar · View at ScopusJ. Li, X. Shi, F. Gao et al., “Filtration of fine particles in atmospheric aerosol with electrospinning nanofibers and its size distribution,” Science China Technological Sciences, vol. 57, no. 2, pp. 239–243, 2014. View at Publisher · View at Google Scholar · View at ScopusY. Mei, Z. Wang, and X. Li, “Improving filtration performance of electrospun nanofiber mats by a bimodal method,” Journal of Applied Polymer Science, vol. 128, no. 2, pp. 1089–1094, 2013. View at Publisher · View at Google Scholar · View at ScopusJ. Lang, S. Cheng, J. Li et al., “A monitoring and modeling study to investigate regional transport and characteristics of PM2.5 pollution,” Aerosol and Air Quality Research, vol. 13, no. 3, pp. 943–956, 2013. View at Publisher · View at Google Scholar · View at ScopusN. Vitchuli, Q. Shi, J. Nowak, M. McCord, M. Bourham, and X. Zhang, “Electrospun ultrathin nylon fibers for protective applications,” Journal of Applied Polymer Science, vol. 116, no. 4, pp. 2181–2187, 2010. View at Publisher · View at Google Scholar · View at ScopusL. Wang, C. Han, M. N. Nadagouda, and D. D. Dionysiou, “An innovative zinc oxide-coated zeolite adsorbent for removal of humic acid,” Journal of Hazardous Materials, vol. 313, pp. 283–290, 2016. View at Publisher · View at Google ScholarK. Guesh, C. Márquez-Álvarez, Y. Chebude, and I. Díaz, “Enhanced photocatalytic activity of supported TiO2 by selective surface modification of zeolite Y,” Applied Surface Science, vol. 378, pp. 473–478, 2016. View at Publisher · View at Google ScholarP. Vinaches, J. A. B. L. R. Alves, D. M. Melo, and S. B. C. Pergher, “Raw powder glass as a silica source in the synthesis of colloidal MEL zeolite,” Materials Letters, vol. 178, pp. 217–220, 2016. View at Publisher · View at Google ScholarH. Chen, J. Wang, H. Wang et al., “Preparation of stellerite loading titanium dioxide photocatalyst and its catalytic performance on methyl orange,” Journal of Nanomaterials, vol. 2015, Article ID 701589, 6 pages, 2015. View at Publisher · View at Google Scholar · View at ScopusY. M. Chen, J. Q. Wan, Y. W. Ma, W. W. Wu, and Y. Wang, “Effects of pressing and drying on the cellulose crystalline degree of recycled fiber,” China Pulp & Paper Industry, vol. 8, pp. 26–29, 2008. View at Google ScholarC. Da Silva Meireles, G. R. Filho, R. M. N. De Assunçã, M. Zeni, and K. Mello, “Blend compatibility of waste materials—cellulose acetate (from sugarcane bagasse) with polystyrene (from plastic cups): diffusion of water, FTIR, DSC, TGA, and SEM study,” Journal of Applied Polymer Science, vol. 104, no. 2, pp. 909–914, 2007. View at Publisher · View at Google Scholar · View at ScopusD. L. Cheng, S. X. Jiang, and Q. S. Zhang, “The effect and mechanism of cooking on the chemical components of bamboo fibers,” Journal of Bamboo Research, vol. 29, no. 1, pp. 50–53, 2010. View at Google ScholarX. R. Guo and P. Wang, “Simulation of steady collection efficiency of micron wood fiber pits on ultrafine particles,” Journal of Nanjing Forestry University: Natural Sciences Edition, vol. 38, no. 3, pp. 98–102, 2014. View at Publisher · View at Google Scholar


This is a preview of a remote PDF: http://downloads.hindawi.com/journals/ijps/2016/2198506.pdf

Hua Chen, Jian Lou, Fei Yang, Jia-nan Zhou, Yan Zhang, Huabo Yao. Use of Oxalic-Acid-Modified Stellerite for Improving the Filter Capability of PM2.5 of Paper Composed of Bamboo Residues, International Journal of Polymer Science, 2016, DOI: 10.1155/2016/2198506