New twinning route in face-centered cubic nanocrystalline metals

Nature Communications, Dec 2017

Twin nucleation in a face-centered cubic crystal is believed to be accomplished through the formation of twinning partial dislocations on consecutive atomic planes. Twinning should thus be highly unfavorable in face-centered cubic metals with high twin-fault energy barriers, such as Al, Ni, and Pt, but instead is often observed. Here, we report an in situ atomic-scale observation of twin nucleation in nanocrystalline Pt. Unlike the classical twinning route, deformation twinning initiated through the formation of two stacking faults separated by a single atomic layer, and proceeded with the emission of a partial dislocation in between these two stacking faults. Through this route, a three-layer twin was nucleated without a mandatory layer-by-layer twinning process. This route is facilitated by grain boundaries, abundant in nanocrystalline metals, that promote the nucleation of separated but closely spaced partial dislocations, thus enabling an effective bypassing of the high twin-fault energy barrier.

A PDF file should load here. If you do not see its contents the file may be temporarily unavailable at the journal website or you do not have a PDF plug-in installed and enabled in your browser.

Alternatively, you can download the file locally and open with any standalone PDF reader:

https://www.nature.com/articles/s41467-017-02393-4.pdf

New twinning route in face-centered cubic nanocrystalline metals

Abstract Twin nucleation in a face-centered cubic crystal is believed to be accomplished through the formation of twinning partial dislocations on consecutive atomic planes. Twinning should thus be highly unfavorable in face-centered cubic metals with high twin-fault energy barriers, such as Al, Ni, and Pt, but instead is often observed. Here, we report an in situ atomic-scale observation of twin nucleation in nanocrystalline Pt. Unlike the classical twinning route, deformation twinning initiated through the formation of two stacking faults separated by a single atomic layer, and proceeded with the emission of a partial dislocation in between these two stacking faults. Through this route, a three-layer twin was nucleated without a mandatory layer-by-layer twinning process. This route is facilitated by grain boundaries, abundant in nanocrystalline metals, that promote the nucleation of separated but closely spaced partial dislocations, thus enabling an effective bypassing of the high twin-fault energy barrier. Introduction Twinning plays an important role in the plasticity and strengthening of metals and alloys1,2,3,4,5,6,7,8,9,10,11,12,13,14. It also provides possible solutions for enhancing the ductility of structural alloys in high-temperature applications15. In the classical twinning theory for face-centered cubic (FCC) metals, a deformation twin is nucleated through layer-by-layer movement of partial dislocations on consecutive, close-packed atomic planes16,17,18,19 via the pole mechanism16, prismatic gliding17, faulted dipoles18, stimulated slip, and other mechanisms2,3,19,20,21,22. In nanocrystalline (NC) metals, grain boundaries (GBs) can lead to twinning processes that are different from those of coarse-grained counterparts, and many alternative twinning routes, such as GB splitting, heterogeneous and homogeneous twin formation, have been proposed4,21,23. However, it is commonly believed that the classical pathway of twin nucleation should be preserved, i.e., a deformation twin must inevitably be nucleated through the layer-by-layer emission of partial dislocations on consecutive atomic planes without interruption1,2,3,4,5,6,7,8,16,17,18,19,20,21,22,23,24,25,26,27. According to this understanding, deformation twinning should be suppressed in many FCC metals with high unstable twin-fault energy (γutf), such as Al, Ni, Pt, and Pd, in which the formation of twin embryos is difficult7,8,28,29. In addition, it has been recognized that the grain-size effect can lead to a transition of the deformation mechanism from full dislocations to partial dislocations in FCC NC metals2,4,30. The active partial dislocations can increase the likelihood of twinning in NC metals. However, in the theoretical analysis of twinning energy landscape, the initiation of twinning via formation of a layer-by-layer stacking fault (SF) configuration depends not only on the unstable SF energy (γusf) but also, more decisively, on an energy barrier, known as the γutf, and accordingly on the ratio of γutf/γusf (see refs. 5,6). Twinning is, therefore, highly unfavorable in many metals such as Al, Ni, Pt, and Pd, because of their high γutf. However, this theoretical prediction is at odds with an extensive body of experimental observations of deformation twins in these FCC NC metals2,4,8. In this work, we utilized a recently developed technique of nanomechanical testing31 together with a spherical-aberration-corrected transmission electron microscope (Cs-corrected TEM) to capture the atomic-scale twinning process in NC Pt. Our in situ observations provide compelling evidence of a new route of deformation twinning in NC Pt having a high twin-fault energy barrier. This new twinning route features the emission of a partial dislocation between two previously formed SFs separated by one atomic layer, which contrasts with the classical twinning model of layer-by-layer formation of SFs. The new twinning pathway has a much lower energy barrier than the conventional layer-by-layer twinning. Our results thus provide a new mechanistic understanding on the formation of widely observed deformation twins in FCC NC metals with high twinning energy barriers. Results In situ atomic-scale observation of twin nucleation The Pt thin film samples used in this work consist of nano-sized grains. Grain sizes range from 4 to 20 nm with an average value of 10 nm, and most grain sizes are <15 nm30. The in situ atomic-scale tensile experiments were performed with atomically resolved mechanical microscopy (ARMM), which integrates a nanomechanical testing device (see Supplementary Figs. 1–4 and Method) into a Cs-corrected TEM32. Figure 1 shows the high-resolution TEM (HRTEM) images of a twin nucleation process, viewed along the \(\left[ {1\bar 10} \right]\) direction and acquired 0.5 s apart during in situ tensile testing. Figure 1a is an HRTEM image taken prior to the elastic limit and hence no dislocations were observed. Further loading led to the format (...truncated)


This is a preview of a remote PDF: https://www.nature.com/articles/s41467-017-02393-4.pdf

Lihua Wang, Pengfei Guan, Jiao Teng, Pan Liu, Dengke Chen, Weiyu Xie, Deli Kong, Shengbai Zhang, Ting Zhu, Ze Zhang, Evan Ma, Mingwei Chen, Xiaodong Han. New twinning route in face-centered cubic nanocrystalline metals, Nature Communications, 2017, Issue: 8, DOI: 10.1038/s41467-017-02393-4