Ge pMOSFETs with GeOx Passivation Formed by Ozone and Plasma Post Oxidation

Nanoscale Research Letters, Apr 2019

A comparison study on electrical performance of Ge pMOSFETs with a GeOx passivation layer formed by ozone post oxidation (OPO) and plasma post oxidation (PPO) is performed. PPO and OPO were carried out on an Al2O3/n-Ge (001) substrate followed by a 5-nm HfO2 gate dielectric in situ deposited in an ALD chamber. The quality of the dielectric/Ge interface layer was characterized by X-ray photoelectron spectroscopy and transmission electron microscopy. The PPO treatment leads to a positive threshold voltage (VTH) shift and a lower ION/IOFF ratio, implying a poor interface quality. Ge pMOSFETs with OPO exhibit a higher ION/IOFF ratio (up to four orders of magnitude), improved subthreshold swing, and enhanced carrier mobility characteristics as compared with PPO devices. A thicker Al2O3 block layer in the OPO process leads to a higher mobility in Ge transistors. By comparing two different oxidation methods, the results show that the OPO is an effective way to increase the interface layer quality which is contributing to the improved effective mobility of Ge pMOSFETs.

A PDF file should load here. If you do not see its contents the file may be temporarily unavailable at the journal website or you do not have a PDF plug-in installed and enabled in your browser.

Alternatively, you can download the file locally and open with any standalone PDF reader:

https://link.springer.com/content/pdf/10.1186%2Fs11671-019-2958-2.pdf

Ge pMOSFETs with GeOx Passivation Formed by Ozone and Plasma Post Oxidation

Nanoscale Research Letters December 2019, 14:126 | Cite as Ge pMOSFETs with GeOx Passivation Formed by Ozone and Plasma Post Oxidation AuthorsAuthors and affiliations Yang XuGenquan HanHuan LiuYibo WangYan LiuJinping AoYue Hao Open Access Nano Express First Online: 05 April 2019 67 Downloads Part of the following topical collections:Applications of Atomic Layer Deposition Abstract A comparison study on electrical performance of Ge pMOSFETs with a GeOx passivation layer formed by ozone post oxidation (OPO) and plasma post oxidation (PPO) is performed. PPO and OPO were carried out on an Al2O3/n-Ge (001) substrate followed by a 5-nm HfO2 gate dielectric in situ deposited in an ALD chamber. The quality of the dielectric/Ge interface layer was characterized by X-ray photoelectron spectroscopy and transmission electron microscopy. The PPO treatment leads to a positive threshold voltage (VTH) shift and a lower ION/IOFF ratio, implying a poor interface quality. Ge pMOSFETs with OPO exhibit a higher ION/IOFF ratio (up to four orders of magnitude), improved subthreshold swing, and enhanced carrier mobility characteristics as compared with PPO devices. A thicker Al2O3 block layer in the OPO process leads to a higher mobility in Ge transistors. By comparing two different oxidation methods, the results show that the OPO is an effective way to increase the interface layer quality which is contributing to the improved effective mobility of Ge pMOSFETs. KeywordsGermanium Passivation Ozone Plasma Post oxidation Metal-oxide-semiconductor field-effect transistor (MOSFET)  Abbreviations Al2O3 Aluminum oxide ALD Atomic layer deposition BF2+ Boron fluoride ion EOT Equivalent oxide thickness Ge Germanium GeOx Germanium oxide HF Hydrofluoric acid HfO2 Hafnium dioxide TEM Transmission electron microscope MOSFETs Metal-oxide-semiconductor field-effect transistors OPO Ozone post oxidation PPO Plasma post oxidation Qinv Inversion charge density SS Subthreshold swing XPS X-ray photoelectron spectroscopy μeff Effective hole mobility Background With conventional complementary metal-oxide-semiconductor (CMOS) devices approaching its physical limit, performance enhancement is hard to realize for high-speed semiconductor devices with silicon (Si) as the channel material. Replacing substrate or channel material with other material with high mobility is an imperative option. Germanium (Ge) has been considered as a promising alternative channel material owing to higher carrier mobility than that of Si. The MOSFET usually needs a high-quality oxide/semiconductor interface to reach high effective mobility. However, for quite a long history, Ge MOSFETs suffered from the high interface state density (Dit) caused by the poor thermal stability of GeO2 and dangling bonds [1]. Thus, plenty of research has been carried out on Ge interface passivation. Several approaches to achieving a high-quality Ge/dielectric interface layer have been reported, such as Si passivation by uniformly depositing several Si monolayers on Ge substrate before dielectric epitaxy or self-passivation by forming GeO2 on purpose [2, 3]. In order to form a high-quality GeO2 layer, there are many oxidation processes to reduce Dit and improve thermal stability including high-pressure oxidation [4], ozone oxidation [5], H2O plasma [6], and electron cyclotron resonance (ECR) plasma post oxidation [7]. In recent years, plenty of works have been reported that high-performance Ge MOSFET can be realized by post oxidation through Al2O3/Ge interface. In 2014, a Ge CMOS inverter was realized on a Ge-on-insulator (GeOI) substrate with GeOx grown by rapid thermal annealing in pure oxygen ambient after 1 nm Al2O3 was deposited on Ge [8]. In ref. [7], Ge pMOSFETs and nMOSFETs with GeOx passivation were fabricated with oxygen plasma post oxidation and temperature dependence of GeOx thickness and electrical performance were also discussed. Thermal oxidation of Ge by ozone can be performed at a lower temperature, for ozone is more reactive than oxygen [5]. The impact of temperature on GeOx thickness grown by ozone on Ge surface was demonstrated. Ge pMOSFETs with GeOx passivation fabricated by ozone post oxidation was also reported [9]. In this work, Ge pMOSFETs with GeOx passivation are fabricated using ozone post oxidation (OPO) and oxygen plasma post oxidation (PPO) of the Al2O3/n-Ge interface. A comparison study on the electrical performance of Ge pMOSFETs with OPO and PPO is carried out. All the processes except passivation are precisely controlled to be the same. The post oxidation was carried out after the Al2O3 block layer deposition that is different from [9] in which the post oxidation was after HfO2 deposition. The mobility degeneration mechanism of Coulomb and roughness scattering is investigated. The impact of the thickness of the Al2O3 block layer on device performance is also discussed. Overall, we demonstrate that OPO is a promising passivation technique for future Ge MOSFET fabrication. Methods Ge pMOSFETs were fabricated on 4-in. n-Ge (001) wafers with a resistivity of 0.14–0.183 Ω cm. Three different passivation processes were performed, and the key process steps are shown in Fig. 1a. The wafers were cleaned by diluted HF (1:50) and deionized water for several cycles to remove the native oxide and then transferred into a plasma-enhanced atomic layer deposition PEALD (Picosun R200 Advanced) chamber immediately. Then, a thin Al2O3 film (~ 1 nm) was deposited at 300 °C with trimethylaluminium (TMA) and deionized water (H2O) as the precursors of Al and O, respectively. Because the Al2O3/GeO2 layer is too thin to have a precise oxygen atom ratio, we marked these two layers as AlOx/GeOx. PPO was performed with the Litmas remote plasma source for 60 s. An ozone generator (IN USA AC series Ozone generators) with the input oxygen flow of 750 sccm was used for the OPO treatment in 50% O3/O2 ambient. Without breaking the vacuum, 60-cycle HfO2 was then deposited on the top of AlOx/GeOx after PPO or OPO treatment at 300 °C using tetrakis dimethyl amino hafnium (TDMAHf) and H2O as the precursors of Hf and O, respectively. A 100-nm TaN was then deposited by reactive sputtering as gate metal. After gate patterning and etching, self-aligned BF2+ implantation into source/drain(S/D) regions with an energy of 20 keV and a dose of 1 × 1015 cm− 2 was carried out. A 20-nm Ni S/D metal was deposited and patterned by a lift-off process. Finally, rapid thermal annealing at 450 °C for 30 s for dopant activation and S/D ohmic contact was followed. The schematic and microscopy images of the fabricated Ge pMOSFETs are shown in Fig. 1b and c, respectively. Open image in new window Fig. 1 a Key process flow for fabricating Ge pMOSFETs with GeO2 surface passivation with three different passivation methods. b Schematic and c microscope images of the fabricated Ge transistor The cross section of TaN/HfO2/AlOx/GeOx/Ge gate stack was depicted using a transmission electron microscope (TEM) to compare the impact of oxygen plasma or ozone on GeOx formation. Figure 2a and b show the cross-sectional TEM images of TaN/HfO2/AlOx/GeOx/Ge gate stack with PPO and OPO, respectively. The thickness of the amorphous HfO2 layer in both devices is 6 nm. Wafer A with 60s PPO treatment have a distinct AlOx/GeOx layer between the HfO2 and Ge substrates. This AlOx/GeOx layer in wafer B formed by 20 min OPO has an untidy margin. The thickness of the GeOx layer is in accordance with the data in [10]. Open image in new window Fig. 2 Cross-sectional TEM images of the high-k/metal gate stack with a AlOx/GeOx interfacial layer (IL) fabricated by a OPO and b PPO on a n-Ge (001) channel Results and Discussion The output and transfer characteristics coupled with high-frequency gate-to-source capacitance-voltage (CV) were measured by Keithley 4200-SCS. Figure 3 shows the comparison of transfer and output characteristic of Ge pMOSFETs with three different formation conditions of the AlOx/GeOx passivation layer. All the devices on various wafers have a gate length (LG) of 3 μm. Devices on wafer A exhibit a higher saturated drain current (IDS) compared to the other two wafers. But wafers B and C with OPO show a much lower OFF-state current (IOFF) compared with wafer A with PPO. It is also seen that wafers B and C with OPO worked in enhancement mode and wafer A worked in depletion mode. It is inferred that, after PPO treatment, the n-Ge surface still remains to be p-type due to the high Dit value which has been discussed in [11]. Wafer C with a thicker Al2O3 block layer shows a positive VTH shift compared with wafer B and a higher Dit than wafer B. It is observed from the output characteristics shown in Fig. 3b that, under a low gate voltage (VGS), wafer A has a lower IDS over wafers B and C due to the less-steep subthreshold swing (SS). When the VGS increases, IDS of wafer A is getting higher in comparison with the other two devices. Therefore, from Fig. 3 and TEM images in Fig. 2, the diffusion of the AlOx/GeOx layer may suppress the IOFF, thus resulting in an improvement of passivation effects. Open image in new window Fig. 3 a IDS–VGS and b IDS–VDS characteristics of Ge pMOSFETs with a Al2O3/GeO2 passivation layer fabricated by PPO (wafer A) and OPO (wafers B and C) Figure 4 summarizes the statistical results of the ION/IOFF ratio and subthreshold swing of the devices on different wafers. Ge pMOSFETs with OPO exhibit a higher ION/IOFF ratio (~ 4 orders of magnitude) and remarkably improved SS in comparison with PPO device, indicating a higher quality of the dielectric/channel interface. When compared with wafer B, wafer C exhibits a higher ON-state current (ION) but a lower ION/IOFF ratio. Open image in new window Fig. 4 Statistical plots of a SS and b ION/IOFF ratio for Ge pMOSFETs with different passivation conditions To further represent the interfacial layer quality of different post oxidation methods, wafers A, B, and C (dummy samples without HfO2 and Gate metals) were tested by X-ray photoelectron spectroscopy (XPS). XPS measurement was carried out on three post oxidation dummy samples after PPO or OPO treatment without HfO2 deposition and TaN sputtering. The stoichiometry of GeOx in Al2O3/GeO/Ge samples was investigated with a monochromatic soft Al Kα (1486.6 eV) X-ray source. Ge 3d peaks and peak-differentiating analysis are shown in Fig. 5. The Ge 3d5/2 peak of the three samples is unified at 29.7 eV, and the chemical shifts of Ge 3d3/2, Ge1+, Ge2+, Ge3+, and Ge4+ to Ge 3d5/2 are set to 0.6, 0.8, 1.8, 2.75, and 3.4 eV, respectively [12]. In Fig. 5b, wafer A shows that after a 60s PPO, the main Ge valence in GeOx are Ge1+ and Ge3+. A similar Ge valance state distribution is observed in wafer C, and a Ge3+ component is slightly increased. In Fig. 5b, wafer B shows that an OPO device with thinner (10 cycles) Al2O3 will further oxidize Ge1+ into Ge2+, Ge3+, and Ge4+, while Ge1+ is significantly reduced. Open image in new window Fig. 5 a Ge 3d XPS spectra of Al2O3/GeOx/Ge formed by different conditions. b Peak fittings of the Ge 3d XPS spectra from the GeO2 layer for the three samples The gate-to-source CV characteristics are shown in Fig. 6. From the 1-MHz CV curve, the Dit near midgap is estimated by Terman’s method [13], and an equivalent oxide thickness (EOT) value is also evaluated as listed in Table 1. Twenty-minute OPO (wafers B and C) results in a higher EOT as compared with PPO (wafer A). Wafer C exhibits a higher EOT over that of wafer B, due to the thicker Al2O3 as a blocking layer. It has been reported that the thickness of GeOx on a bare Ge surface in O3 ambient reaches saturation in a few minutes and the saturation thickness is dominated by temperature instead of oxidation time [10]. So in this paper, the thickness of GeOx by ozone post oxidation is saturated after a few minutes and the left oxidation time is only for annealing. Open image in new window Fig. 6 Gate-to-source capacitance versus VGS characteristics of Ge pMOSFETs passivated by PPO (wafers A) and OPO (wafers B and C) Table 1 Calculated properties of Ge pMOSFETs in three passivation conditions   Dit(1012 cm–2 eV−1) EOT(nm) RSD(Ω) RCH(Ω/μm) Wafer A 9.07 1.83 117 32.7 Wafer B 7.91 2.11 162 46.7 Wafer C 7.46 2.13 46.7 40.1 Figure 7 summarizes the total resistance (RT) versus LG of each device in this work. Here, RT is defined as VDS/IDS at VDS = 0.05 V and VGS − VTH = 1 V. The source/drain (S/D) series resistance (RSD) and channel resistance (RCH) can be extracted from the intercept and slope of the linear fitting of RT–LG lines as shown in Fig. 7. The extracted RSD and RCH results are summarized in Table 1. Figure 7 shows that the Ge pMOSFETs with PPO exhibit a lower RSD and RCH which is consistent with the capacitance results shown in Fig. 6. Open image in new window Fig. 7 Total resistance (RT) versus gate length (LG) of Ge pMOSFETs Effective hole mobility μeff was extracted based on a total resistance slope-based approach. In Fig. 8, we compare the μeff of our Ge pMOSFETs with PPO and OPO treatment with those of other reported Ge pMOSFETs [9, 14]. Qinv is inversion charge density in the device channel. Ge pMOSFETs with OPO exhibit a higher peak μeff compared to the devices with PPO. Wafer C with a thicker Al2O3 block layer has a higher peak hole mobility of 283 cm2/V s in comparison with wafer B with the thinner Al2O3. Wafer A with PPO exhibits a lower high-field hole μeff with the devices with OPO, which is attributed to the lower roughness scattering. But, at low field, transistors on wafer A with PPO achieve a lower μeff than the OPO devices due to the higher coulomb scattering [15]. Only a few works about Ge pMOSFETs fabricated by ozone passivation have been reported. Here, a comparison of the key device performance between our devices and the reported Ge pMOSFETs treated with OPO [9, 14] are carried out, and the results are shown in Table 2. It is concluded that wafer C in this work achieves the high-field μeff enhancement and higher ION/IOFF as compared with the reported device treated with OPO. Besides, at a Qinv of 5 × 1012 cm− 2, wafer C demonstrates a 2.37× higher μeff in comparison with the Si universal mobility. The ION of wafer C is slightly lower than that in Ref. [9] which is due to the larger EOT. Open image in new window Fig. 8 μeff versus Qinv of Ge pMOSFETs with different passivation conditions. Ge transistors with 15 cycles Al2O3 + 20 min O3 oxidation (wafer C) exhibit a peak μeff of 283 cm2/Vs. The impact of S/D resistance on μeff extraction was removed by the total resistance slope-based effective channel mobility extraction method [16] Table 2 Key device performance of Ge pMOSFETs in this work vs. other published results with OPO   W/L (μm) EOT (nm) SS (mV/dec.) ION @ VDS = − 0.5 V VGS − VTH = − 0.8 V (μA/μm) ION/IOFF @ VDS = −  0.5 V μeff @ peak (cm2/V × S) μeff @ Qinv = 5 × 1012 cm−2 (cm2/V × S) Ref. [9] −−/5 0.6 85 15.8 ~ 0.9 × 103 417 134 Ref. [14] 400/24 4.0 142 1.73 ~ 2.3 × 103 268 184 This work wafer C 100/3 2.1 144 11.2 ~ 4.8 × 103 283 222 Conclusions Ge pMOSFETs are realized with GeOx passivation, which is formed by OPO or PPO treatment of Al2O3/n-Ge in PEALD. The OPO devices exhibit the better transfer and output characteristics, the higher ION/IOFF ratio, the improved subthreshold swing, and the higher peak μeff compared to the PPO devices. For the 15-cycle OPO process, a thicker Al2O3 layer leads to a higher EOT value and an improved μeff in devices compared to the 10-cycle case. All the results in this work indicate that the OPO is an effective passivation way to achieve a high-quality Ge/dielectric interface and thus can be a promising candidate passivation technique for future Ge MOSFET fabrication. Notes Acknowledgements Not applicable. Funding The authors acknowledge support from the National Natural Science Foundation of China under Grant No. 61534004, 61604112, 61622405, 61874081, and 61851406. Availability of Data and Materials The datasets supporting the conclusions of this article are included in the article. Authors’ Contributions YX carried out the experiments and drafted the manuscript. GQH, YL, HL, YBW, and YX designed the experiments. GQH and YL helped to revise the manuscript. JPA and YH supported the study. All the authors read and approved the final manuscript. Competing Interests The authors declare that they have no competing interests. Publisher’s Note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. References 1. Kita K, Suzuki S, Nomura H, Takahashi T, Nishimura T, Toriumi A (2008) Direct evidence of GeO volatilization from GeO2/Ge and impact of its suppression on GeO2/Ge metal–insulator–semiconductor characteristics. Jpn J Appl Phys 47:2349CrossRefGoogle Scholar 2. Tse K, Robertson J (2006) Defect passivation in HfO2 gate oxide by fluorine. Appl Phys Lett 89:142914CrossRefGoogle Scholar 3. Lee C, Nishimura T, Tabata T, Wang S, Nagashio K, Kita K et al (2010) Ge MOSFETs performance: impact of Ge interface passivation. In: Electron Devices Meeting (IEDM), 2010 IEEE International, pp 18.1. 1–18.1. 4Google Scholar 4. Lee CH, Tabata T, Nishimura T, Nagashio K, Toriumi A (2012) Oxidation rate reduction of Ge with O2 pressure increase. Appl Phys Express 5:114001CrossRefGoogle Scholar 5. Kuzum D, Krishnamohan T, Pethe AJ, Okyay AK, Oshima Y, Sun Y et al (2008) Ge-interface engineering with ozone oxidation for low interface-state density. IEEE Electron Device Lett 29:328–330CrossRefGoogle Scholar 6. Liu L-J, Chang-Liao K-S, Fu C-H, Chen T-C, Cheng J-W, Li C-C et al (2013) Ultralow EOT and high mobility Ge pMOSFETs with in-situ H2O plasma grown GeO2 and HfON gate dielectric. In: VLSI Technology, Systems, and Applications (VLSI-TSA), 2013 International Symposium on, pp 1–2Google Scholar 7. Zhang R, Lin JC, Yu X, Takenaka M, Takagi S (2014) Impact of plasma Postoxidation temperature on the electrical properties of Al2O3/GeOx/Ge pMOSFETs and nMOSFETs. IEEE Trans Electron Devices 61:416–422CrossRefGoogle Scholar 8. Wu H, Conrad N, Wei L, Ye PD (2014) First experimental demonstration of Ge CMOS circuits. In: 2014 IEEE International Electron Devices Meeting, pp 9.3.1–9.3.4CrossRefGoogle Scholar 9. Zhang R, Tang X, Yu X, Li J, Zhao Y (2016) Aggressive EOT scaling of Ge pMOSFETs with HfO2/AlOx/GeOx gate-stacks fabricated by ozone postoxidation. IEEE Electron Device Lett 37:831–834CrossRefGoogle Scholar 10. Wang X, Xiang J, Zhao C, Ye T, Wang W (2017) Oxidation mechanism and surface passivation of germanium by ozone. In: Electron Devices Technology and Manufacturing Conference (EDTM), 2017 IEEE, pp 162–163CrossRefGoogle Scholar 11. Zhang W, Lou X, Xie Z, Chang H (2018) Band bending analysis of charge characteristics at GeO2/Ge interface by x-ray photoemission spectroscopy. J Phys D Appl Phys 52:045101CrossRefGoogle Scholar 12. Wang X, Xiang J, Wang W, Xiong Y, Zhang J, Zhao C (2015) Investigation on the dominant key to achieve superior Ge surface passivation by GeOx based on the ozone oxidation. Appl Surf Sci 357:1857–1862CrossRefGoogle Scholar 13. Terman LM (1962) An investigation of surface states at a silicon/silicon oxide interface employing metal-oxide-silicon diodes. Solid State Electron 5:285–299CrossRefGoogle Scholar 14. Zhou L, Wang X, Han K, Ma X, Wang Y, Xiang J et al (2019) Experimental investigation of remote coulomb scattering on mobility degradation of Ge pMOSFET by various PDA ambiences. IEEE Trans Electron Devices. 66:1669-1674.  https://doi.org/10.1109/TED.2019.2900801 15. Toriumi A, Nishimura T (2017) Germanium CMOS potential from material and process perspectives: be more positive about germanium. Jpn J Appl Phys 57:010101CrossRefGoogle Scholar 16. Niu G, Cressler JD, Mathew SJ, Subbanna S (1999) A total resistance slope-based effective channel mobility extraction method for deep submicrometer CMOS technology. IEEE Trans Electron Devices 46:1912–1914CrossRefGoogle Scholar Copyright information © The Author(s). 2019 Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. Authors and Affiliations Yang Xu1Genquan Han1Email authorView author's OrcID profileHuan Liu1Yibo Wang1Yan Liu1Jinping Ao1Yue Hao11.State Key Discipline Laboratory of Wide Band Gap Semiconductor Technology, School of MicroelectronicsXidian UniversityXi’anPeople’s Republic of China


This is a preview of a remote PDF: https://link.springer.com/content/pdf/10.1186%2Fs11671-019-2958-2.pdf

Yang Xu, Genquan Han, Huan Liu, Yibo Wang, Yan Liu, Jinping Ao, Yue Hao. Ge pMOSFETs with GeOx Passivation Formed by Ozone and Plasma Post Oxidation, Nanoscale Research Letters, 2019, 126, DOI: 10.1186/s11671-019-2958-2